【摘 要】
：
Hierarchically mesoporous silica coated superparamagnetic microspheres with an uniform particle diameter of 750-800 nm and shell thickness of 65-100 nm were synthesized utilizing the surfactant-templa
【机 构】
：
Nano Biomedical Research Center, School of Biomedical Engineering and Med-X Research Institute, Shan
【出 处】
：
2011中国功能材料科技与产业高层论坛
论文部分内容阅读
Hierarchically mesoporous silica coated superparamagnetic microspheres with an uniform particle diameter of 750-800 nm and shell thickness of 65-100 nm were synthesized utilizing the surfactant-templated coating process using ethanol as cosolvent and CTAB as surfactant.The obtained materials were highly magnetic with large saturation magnetization.Hierarchically mesoporous silica shell structures were obtained with the aid of organic swelling agent TMB at the TMB/CTAB molar ratios above 0.6.Three kinds of porosities with peak pore sizes of 3.3 nm,5.3 nm,and that larger than 10 nm coexisted in the mesoporous shell due to the inhomogeneous distribution of TMB in CTAB micelles and disordered packing of mesophase by the influence of ethanol.The surface area gradually decreased and the total pore volume first decreased then increased with the increase of TMB/CTAB molar ratio.These hierarchically mesoporous silica coated superparamagnetic microspheres are believed to be highly potential in magnetic targeted delivery of multiple biomolecules with different molecular sizes.
其他文献
本文以聚碳硅烷(PCS)为原料,采用静电纺丝技术制备了β-SiC/SiO2微米纤维,着重探讨了在料液中添加四丁基溴化铵/N,N-二甲基甲酰胺(TBAB/DMF)溶液对前驱体纤维形貌的影响,优选了前驱体的不熔化处理时间,研究了β-SiC/SiO2纤维的光致发光性能.采用扫描电镜(SEM)、傅立叶红外光谱(FT-IR)、X射线粉末衍射(XRD)和光致发光光谱(PL)等测试手段对产物进行了表征.结果表明
P-type Bi0.5Sb1.5Te3 thermoelectric crystals with various percentage of Te (x=0.00-3.00 wt.%) were prepared by gradient freeze method.By doping Te content differently and fabrication processes,the ant
Anatase TiO2 particles of about 20 nm in the diameter were successfully synthesized with Ti(SO4)2 as titanium source and stronger ammonia water as precipitant at 240℃ for 48 h with pH=5 using the hydr
MoO3 submicrobelts with the radial direction of less than 500 nm were successfully synthesized with ammonium paramolybdate as molybdenum source and nitric acid as precipitant at 240 ℃ for 48 h with pH
在不同压紧压力条件下得到不同装填密度的改性纤维球与纤维球过滤器,本文对纤维球过滤器和金属多孔膜去除油气田回注污水中油份和悬浮物进行了研究.实验结果表明在相同压紧压力下改性纤维球装填密度、吸附原水量明显大于未改性纤维球,且高密度的改性纤维球表现出去除油份能力显著,但去除悬浮物效果不明显,金属多孔膜表现出稳定的去除油份及悬浮物的能力.
本文采用挂浆法和粉末冶金工艺制备镍基合金空心球.探讨了原始合金粉末、造孔模板、粉浆粘度、烧结工艺等对空心球的结构形成的影响规律.实验结果表明,非球形粉末的原始粒度越小,毛坯球表面越均匀、光滑,球壳壁厚越薄,烧结后空心球壳孔隙率越少,强度越高;直径约为3mm的聚苯乙烯球有利于制得球壳均匀、孔隙率较低的空心球;粘结剂的浓度越大、液固比越大,涂覆的毛坯球的壁厚也就越大,不同浓度的粘结剂选择合适的液固比,
纳/微米结构功能及其复合材料在锂离子电池、催化、驱动器件、传感器、智能变色窗口与器件,超级电容器等领域有许多重要的应用.为获得性能调控,具有特异形貌纳/微米结构功能及其复合材料适用于不同领域的应用,采用水热方法制备了可控形貌的低维钒氧化物.考察了数种典型软模板的存在对其形貌的影响.采用扫描电镜(SEM),透射电镜(TEM),X-射线衍射(XRD),傅里叶红外(FTIR)等进行了相应表征.结果表明,
Barium ferrite microfibers/poly (vinylidene fluoride) (BaFe12O19/PVDF) composite films were prepared by the solution casting process.The X-ray diffraction analysis indicates the BaFe12O19 microfibers
K2Ti6O13 whiskers (KTOw,0~1.5 wt%) toughened (Pb0.70Ba0.26Sr0.04)(Zr0.52Ti0.48)O3 (PBZT) ceramic composites were prepared by the solid state reaction method.Their structure,mechanical,piezoelectric pr
采用水稀释法研究丙烯酰胺(AM)反相微乳液相区,然后紫外光照引发聚合生成聚丙烯酰胺(PAM)微胶乳,再对其改性制得PAM反应性微凝胶.对产物的结构和形貌进行了表征,并探讨了其作用机理.稳定的反相微乳液外观澄清透明,离心后不分层,PAM反应性微凝胶粉末为球形或类球形,具有明显的团聚现象,颗粒粒径在200nm～400nm之间,其作为交联剂质量分数在0.9％～1.1％时,交联产物韧性较好.