【摘 要】
：
Rod-like silicate particles (attapulgite, ATT) were washed with deionized water and dried, ground and dried.Triethoxy(ethynyl) silane was used to modify ATT
【机 构】
：
Key Laboratory of Specially Functional Polymeric Materials and Related Technology,East China Univers
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
Rod-like silicate particles (attapulgite, ATT) were washed with deionized water and dried, ground and dried.Triethoxy(ethynyl) silane was used to modify ATT to obtain PSA/ATT nanocomposites.Both pristine ATT and organic modified ATT (OMATT) were homogeneously dispersed in a silicon-containing polyarylacetylene resin (PSA).
其他文献
Silicon-containing arylacetylene resin (PSA) has excellent heat resistance, dielectric properties, and low molten-state viscosity for RTM process, which wou
Carbon fiber prepreg have many characteristics ,such as excellent mechanical propertiesa and good process performance, high bonding strength, low shrinkage,
With epoxy resin as matrix, flexible curing epoxy resin system is developed which can be used for sports, and we have studied the performance of composite m
4,4'-Diethynyldiphenyl ether(DEDPE) was synthesized by the Sonogashira reaction of bis(4-bromophenyl) ether with 2-methyl-3-butyn-2-ol and then was used to
Polyarylacetylene is an attractive material due to its excellent high temperature resistant, susceptibility to oxidation at high temperature limits the rang
This paper introduces a flame retardant epoxy resin system.In 0.5h+90℃/90℃/1.5h ,its curing process under curing degree above 85%, oxygen index value is m
A series of low temperature curing polytriazole resins were designed and prepared from a variety of azides and alkynes through 1,3-dipolar cycloaddition rea
The curing reaction and curing kinetics were studied by differential scanning calorimetry(DSC).Curing reaction curves were tested with different heating-up
Except for its relatively high specific strength, specific stiffness and the ability to tailor their mechanical properties, the 1 to 2 order of damping abil
In order to improve the stiffness of epoxy matrix, polyfimctional epoxy resin was modified with amide acid oligomer, and the high modulus epoxy resin matrix