SmCo6.6Nb0.4纳米片的结构、磁性及磁硬化机制分析
【摘 要】
：
由于具有作为高密度磁记录材料和双相纳米永磁材料的潜能，稀土-过渡族金属纳米颗粒的研究已经引起了研究者的高度关注。具有TbCu7-型晶体结构的SmCo7 合金具有良好的内禀磁性能如高居里温度、高饱和磁化强度和高磁晶各向异性场。
【机 构】
：
北京工业大学,材料科学与工程学院,北京,100124
【出 处】
：
中国物理学会2013年秋季学术会议
【发表日期】
：
2013年11期
其他文献
Tunnel magnetoresistance(TMR)effect in magnetic tunnel junctions(MTJs)with a ferromagnetic/insulator/ferromagnetic sandwich structure is one of fascinating physical phenomenon in the field of spintron
In experiment,the synthesis of pure BiFeO3(BFO)bulk ceramics is quite hard.Meanwhile,the magnetoelectric effect in BFO can allow for the control of the ferroelectric and magnetic domain structures via
Mutiferroic thin films with coupled ferroelectric and ferromagnetic order parameters have attracted tremendous interest because of the potential in realizing new multifunctional devices.
With the aim of synthesizing a new ferromagnetic CoFe-based glassy alloy with a large supercooled liquid region,multi-component alloy ingots with nominal compositions(CoxFe1-x)62Nb8B30(x=0-1)were fabr
Thermal stability, magnetic and mechanical properties of Fe-RE-B-Nb(RE = Gd, Tb, Dy, Ho, Er, Tm)bulk
Magnetic heavy rare earth(RE)elements have a localized magnetic moment(4f electrons),which can significantly interact with the 3d electrons of iron atoms.Therefore,the RE-containing Fe-based metallic
一方面，重费米子超导体的发现，标志着磁性关联诱导库珀配对的非常规超导体成为凝聚态物理研究的热点。另一方面，随后发现的铜基超导体具有非常高的超导转变温度，具有广泛的应用前景，令人更加关注非常规超导体的研究。
Anisotropic Magnetoresistance(AMR)in ferromagnet is a well-known and fundamental issue which is believed to originate from spin-orbit coupling.Most of the previous works about AMR mainly focused on po
Amorphous carbon(a-C)films are drawing a lot of attentions due to its wide applications,such as magnetic sensing,photovoltaic applications,pressure sensing,gas sensing and so on,especially for the mag
新型Ni –Mn 基铁磁性形状记忆合金作为一种多功能材料，近年来一直受到凝聚态物理及材料科学领域的广泛关注。与传统的铁磁性形状记忆合金的各向异性能不同，该类合金的Zeeman 能随磁场的增大将连续增加，达到一定程度后就能驱动马氏体相与母相之间的界面移动，并诱发马氏体变体的退孪、成核与长大，最终全部转变为高温母相，显示出“磁场诱导马氏体相变”这一独特性质[1]。