【摘 要】
：
The Nd-Fe-B permanent magnets are being used in for a wide variety of applications (e.g.voice coil motors for hard disk drives and motors for hybrid/electric vehicles) due to its high energy products
【机 构】
：
School of Material Science and Engineering, Guilin University of Electronic Technology, Guilin,54100
【出 处】
：
第十七届全国相图学术会议暨相图与材料设计国际研讨会
论文部分内容阅读
The Nd-Fe-B permanent magnets are being used in for a wide variety of applications (e.g.voice coil motors for hard disk drives and motors for hybrid/electric vehicles) due to its high energy products [(BH)max] [1-3].However,the applications of Nd-Fe-B permanent magnets are limited at the temperature below 150 K due to their spin reorientation at low temperature [4].On the other hand, the content of Nd is decreasing on earth because this element was exploited from miners but to ignore other light rare earth element.In order to take advantage of resources, Y is regarded as an efficient element to substitute Nd for Nd2Fe14B because crystal structure of Y2Fe14B is related to Nd2Fe14B extremely.Many studies have been reported concerning the magnetic properties and phase relations in the ternary Y-Nd-B system [5-7].Therefore, the understanding of phase equilibria and crystal structures of intermetalic compounds in the Y-Fe-B ternary system is dispensable.
其他文献
次磷酸盐因其特殊的物理化学性质以及在各领域的广泛应用已经引起了越来越多的关注[1].由于次磷酸镁具有还原性,弱酸性以及较高的磷含量等性质[2],次磷酸镁可用作阻燃剂、化学镀镍助剂以及土壤改良剂等,除此之外次磷酸镁对治疗风湿性关节炎以及对肥胖人群具有减肥效果[3].为了得到纯度更高、可食用的次磷酸镁,现有两种方法：可用氯化镁与次磷酸钠转化来制备.转化法生产次磷酸镁工艺的设计、优化及控制需要相平衡数据
针状的Ul-Al2MgSi2和U2-Al4Mg4Si4沉淀相在Al-Mg-Si合金时效强化晚期形成。本工作采用分子动力学模拟来研究铝基体包覆下U1和U2亚稳相的微结构演化,同时确定弛豫后所形成新相的晶体结构。模拟结果表明,在达到平衡的过程中,U1纳米线中的铝原子倾向于偏聚,而U2纳米线中的铝原子倾向于被挤出纳米线。不同的形变行为会对铝基体施加不同的应力场,从而影响局部应力集中。此外,通过对比径向分
600 ℃ isothermal section of the Al-Cr-Zn system has been determined by Scanning Electron Microscopy-Energy Dispersive X-ray spectrometry (SEM-EDS), and X-ray Diffraction (XRD).Eleven three-phase regio
杂质和拓扑缺陷对金属间化合物材料的性能有很大的影响.近年来科研工作者对从实验和模拟方法对有序B2-FeAl进行大量研究有利于深入了解铁铝金属间化合物强化和韧化过程的机理,从而为设计制造高强度铁铝金属间化合材料.本文利用LAMMPS和MS模拟软件结合EAM势、NEB方法对B缺陷在B2-FeAl块体、(100)、(110)表面和∑5(310) [001]界面的缺陷形成能和扩散性质进行模拟计算.计算结果
作为镁合金中新型强化相,长周期有序(Long-Period Stacking Ordered, LPSO)结构是目前镁金研究的一个热点[1]。已发现很多Mg-TM-RE合金中具有LPSO相, 而且其在合金强化方面具有重要作用[2]。同时还发现,LPSO堆垛结构随合金化、形成方式以及存在温度等不同而变化[3,4],然而关于稳态的LPSO相结构、相成分以及不同堆垛LPSO的相转变还不够清楚。
The rare-earth (RE)-transition metal compounds have been investigated because of their interesting magnetic properties.Especially, the stable intermetallic compounds in the RE-Mn-X(X=Si, Ge etc) have
本文利用X射线粉末衍射、扫描电子显微镜、能谱分析和金相分析等方法研究并测定了Co-Mn-Sn三元系合金相图富Co区(Co＞ 50 at.％)在873K的合金相关系.实验结果表明,该体系在873K时存在Co3Sn2、CoSn、C02MnSn等3个化合物.Co-Mn-Sn富Co区(Co＞ 50 at.％)在873K的等温截面由6个单相区,9个两相区和4个三相区组成.Mn在α-Co中固溶范围为25-45
次磷酸铝是一种新型的阻燃剂,由于其含磷量高[1]、机械性能好等特点,因此得到广泛应用[2].高纯度的次磷酸铝可以通过次磷酸钠与硫酸铝转化制的[3-5].这方面的研究需要相关相图的支持[6].关于该体系相平衡的研究文献中未见相关报导.为此本论文利用等温溶解平衡法[7]确定了298.15K下Al3+,Na+//H2PO2-,SO42--H2O四元交互体系固液相平衡关系,并绘制了相图.具体实验结果如下：
大多数材料随着温度的升高会膨胀,而一些物质却会产生负热膨胀现象(NTE),即体积随温度升高收缩,温度降低却膨胀.研究较多的主要集中在氧化物中,如ZrW2O8及其类似物,沸石等包含M-O-M型桥氧连接的晶体,由于升温过程中桥氧原子的横向振动使得M-M之间的距离减小,从而产生负热膨胀性.我们组新近对MOFs材料展开了NTE研究,结合变温粉末同步辐射等手段发现了一例在三维方向的负热膨胀化合物.MIL-6
采用高分辨同步辐射X射线粉末衍射和Rietveld全谱拟合法精细修正四方钨青铜结构化合物BaBiNb5O15和Ba2CeFeNb4O15的晶体结构。发现BaBiNb5O15中存在1/3的A位置为空位,这是目前发现四方钨青铜体系中,A位置空位最多的化合物,Bi原子由于6S2孤对电子的影响在A的五角孔隙中存在多重劈裂。通过交流阻抗谱法发现BaBiNb5O15表现较好的氧离子导电特性,A位大量金属离子缺