【摘 要】
：
Cementitious material is one of the potential substrates for widely practical application of photocatalysis.The loading effect and photocatalytic performance were investigated by loading nano-TiO2 on
【机 构】
：
State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
Cementitious material is one of the potential substrates for widely practical application of photocatalysis.The loading effect and photocatalytic performance were investigated by loading nano-TiO2 on the porous magnesium oxychloride cement in different hydration periods.Nano-TiO2 were loaded on 7d, 14d, 21d, 28d hydrated porous magnesium oxychloride cement by vacuum negative pressure method.The results show that the cement based photocatalytic material presented high photocatalytic efficiency.In middle and later cement hydrated period, the needle shape crystal of phase 5 grew well, which benefit the surface nano-TiO2 photocatalyst dispersing into the interspace of phase 5 and the combination between the photocatalyst and the phase 5.
其他文献
Reduced CO2 emission and increased energy saving as well as potential use of several industrial by-products as components of clinker-generating raw mix are well-recognized features associated with cal
Alkali-activated aluminosilicate material, geopolymer, has been expected to be an alternate material for concrete.In this study, fly ash was activated only by alkali hydroxide solution with autoclave
The setting process of the Alkali Activated Cement (AAC) generally is too rapid to be handled at the building site;to prolong the setting time of this type of cement is a key issue of its application.
The application of alkali-activated slag(AAS) has been restricted by its high drying shrinkage.In this paper,effects of CSA type expansion agent, CaO type expansion agent and shrinkage-reducing agent
The transformation process of clay minerals into pozzolanic products for use as active additives in cement matrixes has been closely studied by both the scientific community and the cement industry.So
Future cements will require new constituents in order to become a more sustainable construction product.Therefore, the durability of the cements made with them must be checked.In this respect, coal bo
Pastes with water-cement ratios of 0.3, 0.35, 0.4 and 0.45 were prepared for measuring the chemical shrinkage (CS), the autogenous shrinkage (AS) and the electrical resistivity (ER, p) during hydratio
Effects of polycarboxylate (PCE) superplasticizers with different densities of carboxylate groups, functional group contents, molecular weight, and side chain polymerization degrees on the hydration b
Compared with the added gypsum, protogenetic anhydrite is those anhydrite in clinker and admixture.And using protogenetic anhydrite as setting retarder instead of added gypsum to make cement could be
This paper presents results from the analysis of the first 48 hours of the hydration of three high-volume blended BFS-PC systems.This work has been carried out on the I11 beamline of the Diamond Light