Inhibition Behavior and Mechanism of Calcium Lignosulfonate on Steel in Simulated Concrete Pore Solu

来源 :国际腐蚀工程大会(ICEC2016) | 被引量 : 0次 | 上传用户：ineedtoxiazai

【摘 要】

：

Potentiodynamic polarization measurements,microscopy infrared imaging(M-IR)and X-ray photoelectron spectroscopy(XPS)were used to study the inhibition behavior of calcium lignosulfonate(CLS)on Q235 ste

【作 者】

：

Yishan Wang Yu Zuo 

【机 构】

：

School of Materials Science and Engineering,Beijing University of Chemical Technology,Beijing 100029

【出 处】

：

国际腐蚀工程大会(ICEC2016)

【发表日期】

：

2016年10期

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　Potentiodynamic polarization measurements,microscopy infrared imaging(M-IR)and X-ray photoelectron spectroscopy(XPS)were used to study the inhibition behavior of calcium lignosulfonate(CLS)on Q235 steel in 0.1 mol/L NaCl+Ca(OH)2 solution.

其他文献

Effect of surface pretreatments of aluminum alloy 6061 on corrosion resistance of zirconium-based co

Zirconium-based conversion coating(ZrCC)with chromium-free was successfully prepared on aluminum alloy 6061(AA6061).The effects of various pretreatments including the treatment time of alkaline washin

会议

Study on Synergistic Mechanism of Inhibitor Mixture Based on Electron Transfer Behavior

Surfactants play an important role in industrial production and daily life due to their unique interfacial activities.A proper mixture of surfactants will produce synergistic effect,and thus exhibit b

会议

Corrosion resistance of epoxy coating Containing Nano ZrO2 modified by KH-151 Silane on Mg-Li Alloy

Epoxy coatings containing nano ZrO2 modified by vinyltriethoxysilane(KH-151)were prepared by coating method on the Mg-Li alloy surface.The effect of concentration of nano ZrO2 on corrosion resistance

会议

Selective and specific detection of sulfate-reducing bacteria using potentiometric stripping analysi

A fast,sensitive and reliable potentiometric stripping analysis(PSA)is described for the selective detection of the marine pathogenic sulfate-reducing bacterium(SRB),Desulforibrio caledoiensis.

会议

Investigation of Alternating Stray Current Induced Corrosion of High Strength Steel and Coating Dela

Effects of alternating stray current(AC)on the corrosion behavior of high strength steel and the coating delamination at defect areas have been investigated.AC generated by high voltage power transmis

会议

Engineering Application of Cathodic Protection System in Small Diameter Circulating Water Pipes

One thermal power plant which in Fujian,its circulating water pipes is Q235 steel,Cooling water medium is sea water,Pipeline in a complex corrosion environment,The small diameter Circulating water pip

会议

Progress In Silicate Inorganic Zinc-rich Anti-corrosive Coatings

Silicate inorganic zinc-rich coating is a kind of anti-corrosive coatings consisting of one or more silicate as film material and granular or flaky zinc as filler.

会议

Effect of temperature on the 3Cr low-alloyed steel initial corrosion behavior in CO2 solution

The initial corrosion behavior of 3Cr low-alloyed steel in sodium chloride(NaCl)solution with 0.3 MPa CO2 was systematically investigated at various temperatures.

会议

Effect of particle size distribution of oil/water emulsion on corrosion behavior of pipeline steel

Multiphase flow pipelines are very common in oil industry,under high water content conditions,oil-in-water emulsion will be formed in pipelines.At present,the study about the effect of microscopic pro

会议

R & D of New Titanium Alloys Used for Shipbuilding in China

Because of their excellent comprehensive properties,titanium alloys are the ideal structural materials used for shipbuilding.These kinds of alloys have been paid great attentions in China.

会议