【摘 要】
：
Effect of heat-affected zone(HAZ)on spot weldability in automotive hot stamping(HS)steel sheet was investigated for automotive applications.Tensile test was performed on a tensile testing machine at a
【机 构】
：
Department of Mechanical Engineering,National Institute of Technology,Nagano College,716 Tokuma,Naga
论文部分内容阅读
Effect of heat-affected zone(HAZ)on spot weldability in automotive hot stamping(HS)steel sheet was investigated for automotive applications.Tensile test was performed on a tensile testing machine at a crosshead speed of 3 mm/min,using spot welded test specimen(Parallel length: 60 mm,Width: 20 mm,Thickness: 1.4 mm,Tab: 20×20 mm).The spot welding test was carried out using spot welded test specimen with welding current(I)of 6.3 kA to 9.5 kA.Hardness was measured with the dynamic ultra micro Vickers hardness tester.In HS steel,has very high strength of 1 500 MPa,tensile strength(TS)and total elongation(TEl)of the spot welded test specimen of HS steel were lower than those of base metal test specimen.The spot welded test specimen broke in the weld.The Vickers hardnesses(HVs)of base metal and fusion zone of hot stamping steel were around HV500.In addition,the hardness of HAZ was under HV300.The difference of hardness between fusion zone and HAZ was around HV200.The hardness distribution acted as a notch.On the other hand,in dual phase(DP)steel,has low strength of 590 MPa,the TS of spot welded test specimen of DP steel was the same as the base metal test specimen because of the breaking of base metal.The TEl of the spot welded test specimen of DP steel was smaller than that of base metal test specimen.In the spot welded test specimen of DP steel,the hardness of base metal was around HV200 and the fusion zone was around HV500.The hardness distribution did not act as a notch.The difference in hardness between base metal and HAZ acted on a crack initiation at HAZ softening.
其他文献
The differences of microstructure and property of non-quenched and tempered bainitic steel under different finish rolling temperatures was analyzed by the methods of color metallographic,scanning elec
Before being subjected to water quenched,16mm WDL690D steel was heated at 910℃,930℃,950℃and 970℃for 20min,40min and 60min,respectively.Microstructures of these samples after heat treatment were observ
A new V-Ti-Mo complex micro-alloyed hot-rolled high strength sheet steel was developed by controlling a thermomechanical controlled processing(TMCP)schedule,in particular with variants in coiling temp
To develop thickness>60mm,yield strength>550MPa high-strength steel plate,the effects of heat treatment process on the microstructure and mechanical properties of plate specimens were investigated on
Potential benefits of vanadium in heat treated medium carbon bar steels are considered by reviewing examples from several recent studies.Emphasis is placed on microstructural development,strength,and
An new method is proposed to predict in sequence the phase transformation behavior and the depth of the decarburized ferrite layer with simultaneous scaling of a steel during cooling process from the
We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering.Detailed isothermal treatments were made a
690MPa high strength steel with low yield ratio for building structure has been developed successfully by micro-alloying design and thermal-mechanical controlled processing in WISCO.The mechanical pro
In the shipbuilding industry,the welding efficiency of the ship plate not only has a great effect on the construction cost of the ship,but also affects the construction speed and determines the delive
In multi-pass welding process,various thermal cycle of both weld metal(WM)and heat affected zone(HAZ)will be subjected several times.This will make the initial microstructure occur an irreversible tra