【摘 要】
：
A single-mode laser output of 0.75 W near 2 μm was obtained with a slope efficiency of 28.7%with respect to the absorbed pump power when a self-developed double-cladding Tm3+-doped tellurium germanate
【机 构】
：
Shanghai Institute of Optics and Fine Mechanics,Chinese Academy of Sciences,Shanghai 201800,China;Un
【出 处】
：
第八届中国功能玻璃学术研讨会暨新型光电子材料国际论坛
论文部分内容阅读
A single-mode laser output of 0.75 W near 2 μm was obtained with a slope efficiency of 28.7%with respect to the absorbed pump power when a self-developed double-cladding Tm3+-doped tellurium germanate glass fiber laser was pumped byusing a793 nm diode laser.The core glass possesses an infrared cut-off edge reaching~5 μm.The calculated peak emission cross-section of Tm3+ at 1.9 μm was 6.8 × 10-21 cm2.The measured fluorescence lifetime of 3F4 energy level was 2.96 ms.A single-mode double-cladding tellurium germanate glass fiber was fabricated in house by using the rod-in-tube drawing technique.The lasing threshold was 0.56 W and the lasing wavelength was centered at 1968 nn.Spatial beam quality of the fiber was measured and a value ofiM2 =1.36 was obtained.
其他文献
The high-powered alternating current(AC)light-emitting diode(LED)(AC-LED),featuring low cost,high energy utilization efficiency,and long service life,will become a new economic growth point in the fie
Construction of a chip-based optical microcavity from multi-component glass has long been a significant fundamental challenge in the cross field of materials science and photonics.Here we introduced a
Non-invasive temperature sensors based on optical thermometry techniques,such as fluorescence lifetime and fluorescence intensity ratio(FIR)technique,have recently attracted considerable attention [1]
In this research,we reported the molecular-like Ag(ML-Ag)clusters and Eu3+ co-sensitized efficient broadband down-conversion luminescence in oxyfluoride glass,and the Ag nanocrystal enhanced up-conver
Erbium doped bismuthate glasses show a broad 1.55 μm emission band with the full width at half maximum(FWHM)over 100 nm,and thus have been extensively studied as a promising broadband gain medium for
A series of silicate glasses containing alkaline-earth element(AE),with AE=Mg,Ca,Sr,Ba,were prepared in order to investigate the compositional effects on the physical properties of the glasses.An anom
Theglass representing 60Bi2O3-20B2O3-(40-x)TiO2(x=0,5,10,15 and 20mo1%)were prepared by normal melt quenching technique.The optical and structural features have been investigated by DSC,UV-Vis absorpt
硫系玻璃光纤具有优异的中红外透光性、高的光学非线性、良好的热稳定性和化学稳定性,在中红外光传输、分子传感、非线性光学等领域备受关注.最近,我们在硫系玻璃光纤与光纤传像束的制备及应用方面取得了较显著进展.(1)制备了一系列高机械性能低损耗中红外传输硫系玻璃光纤,在激光传输和大气传感等方面得到了实际应用；(2)设计和制备了小芯径阶跃折射率硫系玻璃光纤,以其为非线性介质,采用飞秒激光抽运,获得了覆盖2-
The float process is widely used,since it has excellent quality and productivity,and accompany with low cost,variable production sizing and convenient online processing.Approximately 90%of the world p
The Stark splitting properties of Yb3+atroom temperature in phosphate laser glass werestudied.To enlarge the Stark splitting level,SiO2 as structure formers was added to the simple composition of 60P2