【摘 要】
：
In this study,effects of alloying elements and hot rolling conditions on the final microstructures and the related mechanical properties of the hot-rolled DP780Y steels were discussed.Controlled rolli
【机 构】
：
Steel and Aluminium R&D Department,China Steel Corporation,Kaohsiung,Taiwan,China
论文部分内容阅读
In this study,effects of alloying elements and hot rolling conditions on the final microstructures and the related mechanical properties of the hot-rolled DP780Y steels were discussed.Controlled rolling patterns,especially step cooling temperature and duration time ( sheet traveling time on the runout table),were simulated by thermomechanical simulator for producing DP 780Y steels on a kind of low carbon steel containing higher amounts of Mn and P.Microstructures and quantitative analysis of the volume fractions of the phases and the fracture surface were characterized by the scanning electron microscopy ( SEM),transmission electron microscopy ( TEM) and the image analyzer,respectively.It was found that the alloy contents of Mn and P elements,not only affected the microstructure of ferrite and martensite phase morphologies,proportions and formations,but also affected the performance of the final steel.In addition,increase of the cooling temperature and duration time decreased the yield and tensile strength,but increased the total elongation.The results showed that with the appropriate proportion of the alloy addition and the cooling process control,an optimized combination of high strength and good elongation balance can be obtained.
其他文献
Surface peeling defect occurred in stamping process.QSTE500TM high strength hot-rolled sheet manufactured by Baosteel was applied.A layer of certain substances similar to slag is found underneath the
Determination of the threshold stress intensity for stress corrosion cracking (KIscc) of narrow areas such as weld and heat affected zone ( HAZ) of a weldment is a non-trivial task,because of requirem
Corrosion behaviour of low-alloy steel containing 1% Cr ( 1Cr) with normalized ( ferritic- pearlitic ) and quenched-and-tempered ( tempered martensitic ) microstructures was investigated in CO2 enviro
热挤压是无缝钢管的先进生产工艺，扩孔工序是挤压前准备空心钢坯的重要中间工序,而扩孔时钢坯温度对扩孔工艺有很大影响.通过计算机模拟和现场试验,研究了不同钢坯温度分布在扩孔工艺中的影响,得出的结论是钢坯温度呈径向温度线性变化,并且内表面温度低于外表面温度的温度场形态,有利于扩孔过程中的稳定性;作为影响扩孔精度的关键因素之一,钢坯的温度分布在钢坯内表面温度低于外表面温度的状态下,有利于减小扩孔余料的大小
Recent pipelines have utilized API Grade X-70 or X-80 for onshore installations and typically heavy wall API X-65 0ffshore for deep water offshore pipelines.However several new projects require capaci
The weldability of the commercial duplex stainless steel B2101,B2304,B2205 and B2507 is discussed.Suitable welding methods,filler metals,thermal cycles and proper shielding and root gases are recommen
254SMO is a typical austenitic stainless steel with 6% molybdenum which gives possible poor oxidation resistance property at high temperature.It may affect the hot working of 254SMO.The high temperatu
A new kind of heat-resistant stainless steel 305B is studied on its mechanical properties under high temperatures in this paper.We also use the thermo-dynamic software THERMO-CALC to accomplish the ca
Two casters for stainless steel slab production have been put into production by Baosteel Stainless Steel Co.,Ltd.Since 2004,the annual output of stainless steel slabs reached to 1.35 million tons in
The effects of heat treatment on δ ferrite transformation for austenitic stainless steel billet 00Cr24Ni13 have been investigated.The result shows that the continuous mesh δ ferrite in the billet will