【摘 要】
：
With the exploitation of gas mixed with sulfur,the requirement of hydrogen induced cracking(HIC)resistance for medium carbon vessels serving at environmental with hydrogen sulfide solution become more
【机 构】
：
Shougang Technology and Research Institute,Beijing,Peking,China,100043
论文部分内容阅读
With the exploitation of gas mixed with sulfur,the requirement of hydrogen induced cracking(HIC)resistance for medium carbon vessels serving at environmental with hydrogen sulfide solution become more rigorous.Through the research on HIC,the formation reasons of those are: MnS inclusions,Al2O3 inclusions,P segregation,Bainites and Macro segregation of slab.Thus if these parameters are controlled appropriately,the qualified medium carbon vessels for resistance to HIC steel will be produced.The conclusions are following: the controlled measurements to cleanliness on liquid steel,macro segregation controlled on slab,large reduction at rolling and normalizing are used to produce the HIC resistance vessels.The properties of tensile strength and low temperature impact meet the standard properly.Meanwhile there arent hydrogen induced cracking found in any samples.
其他文献
In the study a low carbon niobium bearing high strength F-B dual phase automobile steel with high hole expansion property has been investigated.Steels of different chemical composition have been inves
Handan Iron and Steel production of high-strength structural car steel QStE500TM thin gauge products using Nb + Ti composite strengthening,with a small amount of Cr element to improve its hardenabilit
This paper reports on the experience with the production of 27/33 mm X80 heavy wall thicknesses,large OD(48”)in Shouqin Steel Co.,Ltd.(SQS).Considering the technology capability of the plate mill in S
Hydrocarbon pipelines transporting compressible products like methane or high-vapor-pressure(HVP)liquids under supercritical conditions can be susceptible to long-propagating failures.As the unplanned
With the increase of wall thickness of pipeline steel,DWTT fracture toughness has become more and more sensitive to production process,including alloy design and processing,so it need more tight and m
Repeated deformation with optimum reductions in roughing mill exceeds the critical amount of strain required for recrystallization to occur.Recrystallization during roughing mill rolling refines auste
Over the past twenty years,significant advances have been made in the field of microalloying and associated application,among which one of the most successful application cases is HTP practice for hea
The susceptibility to hydrogen embrittlement in high strength mooring chain steel with different boron content(0,0.003%,0.008%)were investigated by electrochemical hydrogen charging technique and tens
This paper analyzes precipitation and dislocation strengthening behaviors of a 27mm thick Niobium-bearing Grade X80 steel plate for strain based design line pipe manufacture.The steel is produced by t
Extensive investigations of metallurgical roles played by Nb microalloying in advanced products of seamless steel tube have been carried out.The results show that with Nb microalloyed,the recrystalliz