【摘 要】
：
The backup roll(BUR)is an important part in continuous rolling.The main failure form is wear of its surface.In this paper,to clarify the wear mechanism and find out the effective countermeasures to re
【机 构】
：
Research Institute of Baosteel,Shanghai 201900,China
【出 处】
：
第十届中国钢铁年会暨第六届宝钢学术年会
论文部分内容阅读
The backup roll(BUR)is an important part in continuous rolling.The main failure form is wear of its surface.In this paper,to clarify the wear mechanism and find out the effective countermeasures to reduce the wear loss of BUR,taking samples from the normally off-line backup rolls in 2050 hot strip mill and 1550 cold strip mill of Baosteel,the surface wear morphology is investigated by means of the stereomicroscope,confocal laser scanning microscope,and scanning electron microscope,et al.The results show that the wear mechanism of backup roll is a combination of abrasive and corrosive wear.The hot rolling BUR is mainly of abrasive wear and corrosive wear,while the cold rolling BUR is mainly of abrasive wear.The main countermeasures to decrease the backup roll wear include:(1)strengthened the matrix strength(hot/cold rolling BUR);(2)fine matrix microstructure(hot/cold rolling BUR);(3)minimization of micro segregation(hot rolling BUR);(4)solution of undissolved carbides(hot rolling BUR).
其他文献
For the past decades,rolling models have been applied based on the rolling mill types.There is no unified rolling force/power model in the industrial and academic fields.The original von Karman equati
钢坯定重切割是提高轧材成品率、降低能耗的关键.分析了钢坯图像尺寸精度及钢坯拉速对钢坯定重的影响,构建了钢坯定重切割行为控制体系结构.基于有限状态机原理将切割目标分解为定重切割的任务及动作,以钢坯理论重量、积分重量及预报重量作为行为控制模型各个状态之间转换驱动的条件,自主实现定重切割目标.所构建的模型是对钢坯定重切割自主行为控制进行的有益探索.钢坯定重切割的自主行为控制能力是钢坯切割系统自动化水平的
冶炼产生的夹杂物在冲压拉伸过程中容易暴露导致缺陷,如裂纹、凸点、印痕等缺陷,对加工制品质量影响较大,甚至一些微小的夹杂也是致命的.为了探究此缺陷产生的机理,采用Laser-OES、EPMA 等手段分析夹杂成分及分布,利用凝固定律计算夹杂在钢水中被捕捉的位置,分析夹杂产生的原因.通过研究分析本文的微小夹杂系三氧化二铝类夹杂,推断在连铸浇铸过程中由于侵入式水口结瘤脱落黏附在结晶壳上产生了皮下夹杂,经过
The behavior of secondary phase particles precipitation in micro-alloyed steel in process of continuous casting has been studied by numerical simulation.The secondary phase precipitation possibility w
To simulate edge milling process of the milling machine of a UOE welding pipe line,the geometric models of milling cutters and steel plate were built by Pro/E software,and the virtual milling process
本文采用物理模拟的方法,以水银为实验介质,在板坯连铸过程中,在水口不同程度堵塞以及施加电磁搅拌情况下,采用超声波多普勒测速仪测量了结晶器模型内金属液的流速分布.结果表明:当水口无堵塞时,结晶器内流场为典型的双环流结构;水口堵塞会在结晶器内水口两侧造成严重的非对称流,即堵塞侧射流减小,非堵塞侧射流增大;当水口堵塞达到50％时,堵塞侧上环流消失,在弯月面靠近结晶器窄边处出现流动死区;电磁搅拌能修正由水
Heat treatment quenching machine is one of the key equipments for steel quenching and tempering treatment,whereas water spraying system is an important part of the quenching machine.High pressure outl
BaoVision-WSIS(Wire Surface Inspection System)-Online Surface inspection system(SIS)for high-speed hot wire which is developed by Baosteel is applied in wire factory.High illumination LED lighting and
Model experiments with low melting point liquid metals are an important tool to investigate the flow structure and related transport processes in melt flows relevant for metallurgical applications.We
The safe transport of sour gas requires steels with enhanced hydrogen induced cracking(HIC)resistance.Centerline segregation bands of high hardness microconstituents and non-metallic inclusions are th