Extensive investigations of metallurgical roles played by Nb microalloying in advanced products of seamless steel tube have been carried out.The results show that with Nb microalloyed,the recrystalliz
【机 构】
：
State Key Laboratory of Metastable Materials Science and Technology,Yanshan University,No. 438 Hebei
论文部分内容阅读
Extensive investigations of metallurgical roles played by Nb microalloying in advanced products of seamless steel tube have been carried out.The results show that with Nb microalloyed,the recrystallized austenite grain(RAG)and final ferrite grain of tubular steel are evidently refined even experiencing a piercing and a continuous rolling at very high temperature,and a certain quantity of(Nb,V)(C,N)and(Ti,Nb,V)(C,N)particles form on air cooling.Moreover,for quenching(Q)& tempering(T)treated tubular steels,the nanoscale particles of(Nb,V)(C,N)further precipitate on heating stage of Q at 900-1000oC,leading to a significant refinement of prior austenite grain(PAG)and final martensitic or bainitic packet/block structures,and during subsequent T at 600-700oC,producing an improved resistance to softening.The microalloying with 0.02-0.04wt%Nb in Q&T martensitic OCTGs of 155ksi or higher grades,have produced an adequate combination of ultrahigh strength and good toughness in casings for ultra-deep well and high-collapse services,perforation gun tube and drill pipe,etc.The SSCC resistance of Q&T martensitic OCTGs including C110 casings and SS105 drill pipe has been also evidently improved due to the 0.02-0.04wt%Nb microalloyed.With 0.03-0.05wt%Nb microalloyed and carbon,Ceq and Pcm reduced,an excellent strength/toughness/weldability combination has been achieved in Q&T bainitic line pipe and structural tube of X60-X100.In addition,the N80_1 class OCTGs with 0.24wt%C-0.02wt%Nb in hot rolling delivery has an improved and qualified mechanical property.
其他文献
Effect of rare earth element Ce on behavior of high temperature deformation of IF steel was discussed.Different Ce content in IF steel were heated to 1250℃ for 5 min with a heating rate of 10/s at vac
In the study a low carbon niobium bearing high strength F-B dual phase automobile steel with high hole expansion property has been investigated.Steels of different chemical composition have been inves
Handan Iron and Steel production of high-strength structural car steel QStE500TM thin gauge products using Nb + Ti composite strengthening,with a small amount of Cr element to improve its hardenabilit
This paper reports on the experience with the production of 27/33 mm X80 heavy wall thicknesses,large OD(48”)in Shouqin Steel Co.,Ltd.(SQS).Considering the technology capability of the plate mill in S
Hydrocarbon pipelines transporting compressible products like methane or high-vapor-pressure(HVP)liquids under supercritical conditions can be susceptible to long-propagating failures.As the unplanned
With the increase of wall thickness of pipeline steel,DWTT fracture toughness has become more and more sensitive to production process,including alloy design and processing,so it need more tight and m
Repeated deformation with optimum reductions in roughing mill exceeds the critical amount of strain required for recrystallization to occur.Recrystallization during roughing mill rolling refines auste
Over the past twenty years,significant advances have been made in the field of microalloying and associated application,among which one of the most successful application cases is HTP practice for hea
The susceptibility to hydrogen embrittlement in high strength mooring chain steel with different boron content(0,0.003%,0.008%)were investigated by electrochemical hydrogen charging technique and tens
This paper analyzes precipitation and dislocation strengthening behaviors of a 27mm thick Niobium-bearing Grade X80 steel plate for strain based design line pipe manufacture.The steel is produced by t