【摘 要】
：
T4 process of cold rolled strip in the floater-type furnace has high heat transfer efficiency.In order to study the rapid characteristic, heat transfer equation of strip in floater-type furnace is est
【机 构】
：
The state key Lab of Rolling and Automation, Northeastern University, China
【出 处】
：
15th International Conference on Aluminium Alloys(ICAA15)(第十
论文部分内容阅读
T4 process of cold rolled strip in the floater-type furnace has high heat transfer efficiency.In order to study the rapid characteristic, heat transfer equation of strip in floater-type furnace is established and the coefficient of convection heat transfer of 6mm thickness strip surface is calculated by finite difference method.At the same time, the T4 process in floater-type furnace is simulated in laboratory, the experimental plates thickness are 1mm and 6mm.
其他文献
AlCu-based alloys have important applications as high-strength and lightweight materials for the fuselage in aviation (AlCuMg, AlCuLi) and as cast-alloys (AlSiCu) for engine blocks in the transport se
Microstructural examination of the Al-5.3Mg-2.4Si-0.6Mn-1.0Fe alloy in the die-cast condition revealed that a significant number of the primary α-AlFeMnSi intermetallic particles were found inside bot
Voids in aluminium can significantly affect materials performance and a key question is their evolution.We characterised the shrinkage of voids in quenched pure aluminium by performing in-situ anneali
The effects of Sn addition on clustering and age-hardening behavior in an Al-0.6Mg-1.0Si (mass ％) alloy were investigated.The specimens were solution treated at 843K and quenched followed by pre-aging
The steering support is the important part because it is high demand for safety, vibration and noise reduction, and as the connection and supporting the dashboard, various electrical appliances and in
The influence of modes on heat treatment of ingots and semi-finished products from alloys A1-Mg-Sc and Al-Cu-Li systems on the structure, phase composition and grain structure was studied.The EBSD dat
The microstructure evolution during the homogenization heat treatment of Al-Mg-Si-Fe-Mn, or AA6xxx, alloys has been investigated using a combination of modelling and experimental studies.The model is
One of the main goals in this work has been to maintain initial material strength, while keeping the added solute level to a minimum.It was found that replacing some Mg and Si with Li in a lean Al 606
In this study, the microstructural evolution of an as-cast AA3105 aluminium alloy during homogenization treatment was simulated with the ClaNG model.The simulated data were compared with experimental
Although several investigations on thermodynamic modelling in Al-Mg alloys were carried out, all previous thermodynamic descriptions have not been able to calculate the metastable phase diagrams of or