【摘 要】
：
Inhibition effects of three new designed triazolyl acylhydrazone derivatives on copper corrosion in 1 M NaCl solution under wet-dry cycle conditions were evaluated via various electrochemical techniqu
【机 构】
：
Key Laboratory of Marine Environmental Corrosion and Bio-fouling,Institute of Oceanology,Chinese Aca
【出 处】
：
第十届海峡两岸材料腐蚀与防护研讨会
论文部分内容阅读
Inhibition effects of three new designed triazolyl acylhydrazone derivatives on copper corrosion in 1 M NaCl solution under wet-dry cycle conditions were evaluated via various electrochemical techniques, SEM, and FTIR.
其他文献
In practice engineering, defects were inevitable for protective coating systems on steel surface.In this paper, a composite coating system, including primer, middle coat as well as top coat, were used
钢筋混凝土腐蚀,特别是海洋环境下的钢筋混凝土腐蚀,会严重破坏工程结构的稳定性.因此,发展无损现场测试技术对了解实际过程的腐蚀影响,并建立有效的方法来提高钢筋混凝土结构的服务寿命尤为重要.
采用电化学交流阻抗研究5083铝合金在淡海水交替环境中的腐蚀行为,并对腐蚀过程中的合金形貌和成分,分别采用扫描电子显微镜和能谱进行评价.结果表明,5083铝合金的腐蚀主要以点蚀为主.同时发现其力学性能随着浸泡时间的增加显著下降.淡海水交替环境下的腐蚀行为,与海水环境下相比,更为严重.
AA6082鋁合金極具未來應用潛力,特别有利於交通載具輕量化的普及率與大型無人飛機的機體結構輕量化.故本研究利用放電合金化法製程,純鐵為消耗性電極(負極)而AA6082鋁合金為被加工物(正極);藉由放電電弧產生之高熱量,使純鐵表面熔融消耗而於鋁合金表面形成高硬度Al-Fe/Al-Fe-C金屬間化合物.
本研究加工鎂合金醫療器材進行不同加工條件,觀察加工植入物表面粗糙程度及氧化情形.因鎂合金加工過程容易造成黏刀、纏層及BUE等特性.因此,本研究為改善加工鎂合金之表面粗糙度品質,透過加工製程、進給率、刀具、潤滑及後處理之方法進行探討.
近年來因電動車以及電網储能的需求,國際上對二次電池之研究已成熱門話題,針對二次可充式金屬空氣電池,則包含Fe-air 、 Zn-air與Li-air等這幾種類型.選用鋅空氣電池則具有低成本,安全性高,對環境友善等優點.但二次鋅空氣電池於鹼性電解質中會有鋅金屬自腐蝕及枝晶(Dendrite structure)生成的情況發生,會影響電池的表現,因此本研究選用了五種添加劑:EDTA 、 Tween20
本研究以溶膠凝膠法搭配旋轉塗佈技術於玻璃基板上成長鋁鈦共掺氧化鋅薄膜,研究內容當試改變掺雜前驅物之禯度探討氧化鋅系薄膜之微結構、腐蝕特性並應用於光電化學分解水.
Under the condition of cathodic protection, calcareous deposit is formed on metals surface.Sulfate-reducing bacterial (SRB) are recognized as the most imminent species taking part in microbiologically
在H28/CO2共存体系中,通过静态失重实验、表面张力测试、XPS技术研究了吡啶季铵盐(PB)与十二烷基三甲基溴化铵(DTAB)、十四烷基三甲基溴化铵(TTAB)、十六烷基三甲基溴化铵(CTAB)三种阳离子表面活性剂之间的缓蚀协同效应.
本文使用一種簡單的方法製備了具有自修復功能的形狀記憶複合塗層(SMC),塗層主要基於熱回應的形狀記憶高分子材料(SMP)以及作為癒合劑的巴西棕櫚蠟微球.