【摘 要】
：
The stringer shaped B type non-metallic inclusions in API X80 linepipe steel plates produced through " BOF-LF-RH-Ca treatment" steelmaking route were found mainly of CaO-Al2O3 system with lower meltin
【机 构】
：
School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beij
论文部分内容阅读
The stringer shaped B type non-metallic inclusions in API X80 linepipe steel plates produced through " BOF-LF-RH-Ca treatment" steelmaking route were found mainly of CaO-Al2O3 system with lower melting temperatures,which formed because: ① There existed many small sized liquid inclusions of CaO-Al2O3 system in liquid steel after the secondary refining and Ca treatment.These small inclusions could aggregate to larger ones of 10 - 20 μm in continuous casting and be deformed into stringer shaped inclusions in steel plates during rolling.②The larger sized low melting temperature CaO-Al2O3 inclusions,in Ca treatment,their surface layers could be modified into high melting temperature CaO,CaS or CaO-CaS system,but the centers were still of CaO-Al2O3 system.During rolling,these inclusions could also be elongated to stringer typed ones because of their soft CaO-Al2O3 centers.A new strategy for control of B type inclusions in linepipe steel plates was adopted.The key of the control was shifted from removing low melting temperature inclusions of CaO-Al2O3 system after Ca treatment to removing as much as possible inclusions especially large sized inclusions before the Ca treatment.With the new strategy,amount of inclusions after RH refining was remarkably decreased and the efficiency of Ca treatment significantly improved.The inclusions found in steel plates were all of high melting temperature CaO-CaS system and the severities of B-type inclusions have been lowered from "≤2.0" to "0".
其他文献
The refining process of ultra-pure ferritic stainless steels was studied in laboratory.The effects of Fe-Si-Al alloy with different Si/Al ratio on deoxidation process and the typical inclusions after
Titanium diboride ( TiB2) have been widely studied as one of the most promising engineering ceramics and refractory material because of its excellent physical and chemical properties such as high melt
在脱硫扒渣的过程中,不同批次铁水包扒出的铁水会相互渗透,导致渣铁凝固结成大块,难以破碎,针对这一问题,宝钢集团新疆八一钢铁股份公司第二炼钢厂开发了一种使用炼钢系统自产废料制备脱硫渣阻断剂,使用该阻断剂后不仅降低了脱硫渣的加工处理难度,渣铁回收率达到92％以上,而且减轻了环境污染,予以浅述。
在连铸结晶器保护渣成分范围内制备了CaO-SiO2-Al2O3-Na2O-CaF2五元水淬渣样,在渣样化学成分和Raman光谱检测分析的基础上,计算了熔体结构单元含量,进而讨论了 熔体碱度和Al2O3含量对熔体聚合程度的影响和铝离子的存在形式.结果表明,随着碱度的升高,熔体的NOB/T值增大,聚合程度降低,随着Al2O3含量的升高,熔体的NOB/T值减小,聚合程度升高.熔体中的硅离子主要以Q0\Q
Laboratory investigation on formation of inclusion in Ti-Al complex deoxidized C-Mn steel was carried.The results are as follows : when Al content in steel is very low ( [ Al] = 0.000 5%),0.003% 0.00
连铸坯皮下缺陷对后续热轧钢板表面质量合格率影响较大.应用扫描电镜分析、能谱分析和显微镜技术等分析手段,研究了IF钢铸坯皮下缺陷的类型及形成的起因.该类缺陷发生在热轧卷宽度方向上无明显规律,在轧制延伸过程中造成钢板分层开裂并形成翘皮缺陷.结果表明：大部分缺陷都是夹杂物氧化铝、氧化钙等,同时附有气泡,而单纯是或气泡和保护渣卷入的缺陷很少,与有关文献报道不全一致.结合该钢种的热轧生产数据表明：采用直弧形
This paper study on two process routes of ultra-low sulphur steel,"Hot metal desulphurization-Basic oxygen furnace-Ladle powder injection-LF refining" and " Hot metal desulphurization-Basic oxygen fur
结晶器流动模式影响着铸坯的表面质量，为了获得实际生产实践中结晶器的最佳流动模式,本文利用数值模式方法,研究了不同断面条件下,浸入式水口深度、拉速对结晶器内流动模式的影响,得出了最佳的工艺参数搭配。
Results of work on melting,pouring,forging and heat treatment of 415 ton ingots from steel of 45 H3 MIF as semiproducts for manufacturing of large backup rolls according to order of company《 Severstal
Effects of Mg addition on the solidification macrostructure of Ti-stabilized ultra-purity ferritic stainless steels was evaluated experimentally in order to obtain the fine equiaxed grains.Thermodynam