【摘 要】
：
Two kinds of crystalline and mesoporous alumina samples were prepared using aluminium isopropoxide as precursor and P 123 as template agent.They are labeled OMA-800 and OMA-400 in this paper, and test
【机 构】
：
Faculty of Material Science and Chemistry, China University of Geosciences, Wuhan 430074, PR China
【出 处】
：
中国颗粒学会超微颗粒专委会2013年年会暨第八届海峡两岸超微颗粒学术研讨会
论文部分内容阅读
Two kinds of crystalline and mesoporous alumina samples were prepared using aluminium isopropoxide as precursor and P 123 as template agent.They are labeled OMA-800 and OMA-400 in this paper, and tested for adsorptive removal of fluoride in water.
其他文献
Caries is a multifactorial disease and usually caused by the pH fluctuations in the bacterial plaque fluid.An irreversible demineralization occurs on tooth surfaces, leading to decay and even loss of
莫特绝緣体材料拥有优异的光学和电学性能.在发生半导体-金属相变(莫特相变)时,其红外光的透过率和电阻值发生显著改变,这种特性使其在许多领域都有广泛的应用前景.比如VO2在室温附近发生相变,可以作为热致变色涂层材料、光存储材料、光电开关器件和节能用智能窗材料等等.而相变温度较高的Ti2O3则可以用作高温智能窗、热存储功能材料等等.
本研究使用二氧化鈦/雲母及氮化硼為初始材料,分別經由機械混合及球化技術製備複合粉體.並以亞麻仁油製備乳液,經紫外光-近紅外線分光光度儀及防曬係數測試儀分析,對光學與防曬特性(防曬係數SPF、與臨界波長(Critical wavelength))進行探討,結果顯示,球型化之複合粉體經由粒度分析,其中位徑為(8.8um),相較於奈米二氧化鈦(～20nm)在光學特性上,有較優異的吸收强度.防曬特性方面,
在合适的乙醇—氨化PAA介质中合成超微细碳酸锰前驱体,将前驱体在含氧气氛中先于450℃保温30-45min,再升温至980-1100℃并保温45min,获得高纯超细Mn3O4粉体,通过多种方法进行表征,结果显示其纯度达到99.3％,比表面积达15.6m2/g,晶体粒径＜2um.
This study evaluated high water absorbency and constantly phosphorus release properties of two novel hybrid hydrogel materials as potential hydrogel fertilizers.In this article, the hybrid hydrogel ma
Besides the qualified spectral properties, the commercial phosphors require other qualities such as high luminescent intensity, good powder mobility, well-shaped crystal form and uniform size distribu
Cystinosis and some other diseases are characterized by high concentrations of cystine in urine (usually ＞400 mg L-1).Until now many methods have been developed to detect cystine in human urine, such
有机化学反应通常在反应釜中进行，由于化学物质的粘稠吸附性，使得反应釜中化学物质粘壁成为妨碍正常生产的一个重要问题，本文通过溶胶-凝胶法制备具有低表面能的纳米溶胶，将其喷涂在洁净不锈钢反应釜内外壁，经350℃固化后，能在不锈钢涂料反应釜壁上形成厚度为微米级的不粘涂层。通过在制作涂料的不锈钢反应釜的试验表明，此方法制备的涂层施工工艺和固化工艺简单，防粘效果持久性强，具有良好的应用前景。
In this paper, ordered crystal mesoporous γ-Al2O3 was synthesized by one-step method and it was used to study the adsorption capacity of fluoride in drinking water.A system studies about the adsorptio
Ordered mesoporous alumina (OMA) was synthesized through facile sol-gel method.Adsorption ability of the OMA is evaluated by choosing the methylene blue as an adsorbate,and this material exhibited ext