【摘 要】
：
分别利用等离子喷涂(APS)、超音速等离子喷涂(SAPS)和超音速火焰喷涂(HVOF)工艺,在45#钢基体表面制备WC-10Co-4Cr涂层。分析比较了三种涂层的孔隙率、显微硬度和耐磨性能。结
【机 构】
：
黑龙江科技大学材料科学与工程学院,哈尔滨工业大学材料科学与工程学院,
论文部分内容阅读
分别利用等离子喷涂(APS)、超音速等离子喷涂(SAPS)和超音速火焰喷涂(HVOF)工艺,在45#钢基体表面制备WC-10Co-4Cr涂层。分析比较了三种涂层的孔隙率、显微硬度和耐磨性能。结果表明,SAPS和HVOF制备的涂层性能相当,且相结构单一,与粉末相近;与等离子喷涂相比,这两种工艺所制备涂层的致密度和显微硬度更高,耐磨性能更优异。
WC-10Co-4Cr coatings were prepared on the surface of 45 # steel by plasma spraying (APS), supersonic plasma spraying (SAPS) and HVOF. The porosity, microhardness and wear resistance of the three coatings were analyzed and compared. The results show that the coating prepared by SAPS and HVOF has the same performance and single phase structure, which is similar to that of the powder. Compared with plasma spraying, the coatings prepared by the two processes have higher density and microhardness, more wear resistance Excellent.
其他文献
一定形状的合金在某种条件下，经任意塑性变形，然后加热至该种材料固有的某一临界点以上时，又完全恢复未变形形状的现象，称为形状记忆效应，具有形状记忆效应的合金，称为形状记忆合金
采用粉末冶金工艺制备不同WC含量的Ti(C,N)-xWC-Ni-Mo-C金属陶瓷,通过扫描电子显微镜(SEM)观察了Ti(C,N)-xWC-Ni-Mo-C金属陶瓷组织、断口形貌和裂纹扩展路径。结果表明:Ti(C,
随着线材加工业的发展拉丝机用量愈来愈大，怎样正确地选用和统一拉丝机的规格系列应是当务之急。通过对众多型式拉丝机的对比分析并结合工作经验，对拉丝机的机械结构、电机配备
采用微电子技术改造传统捻股成绳设备，介绍变频技术在股绳机上的应用，使整机综合性能提高，且节能降耗；介绍电子测长仪在股绳机上应用，不仅提高计米精度，而且还能挖掘设备生产潜力；介
目前，进入施工现场的冷轧带肋钢筋，通过质量技术检督部门的抽查结果表明，有相当一部分产品的质量不合格，尤其是伸长率指标不合格，如不改善其质量，将不利于推广应用。 为了控制产
采用石墨粉为碳源分两段还原MoO3粉末,通过对各阶段产物的XRD、FESEM和EDS分析表征,初步探讨还原过程中可能的反应历程。结果表明,Mo4O11可能是碳还原MoO3为MoO2过程中的过渡
采用沉淀转化法,在碱性条件下用葡萄糖(C6H12O6)还原CuSO4得到砖红色的Cu2O,再以Na2S为硫化剂将Cu2O转化成Cu2S,所得Cu2S经不同温度的煅烧制备出非化学计量化合物Cu2 xS.采用
采用灯泵浦YAG-T50系列激光打标机对YG8硬质合金进行了端面螺旋槽微造型加工实验.研究了有效矢量步长、有效矢量步间延时、Q频率、激光电流等工艺参数对微造型加工质量的影响
以废钽料为原料、高碳铁为碳载体,利用熔炼过程的固液扩散反应结合酸洗工艺生产细TaC颗粒,并通过XRD、SEM对产物进行表征.结果表明,熔炼保温过程中C原子与钽料发生扩散反应,
ST255重卷机是钢帘线精卷重排配套设备。传统的重卷设备由于钢帘线在过线轮之间存在打滑现象，致使测量值偏小，高速下定长计数困难，经常出现断丝漏检现象。经对ST255重卷机的改进