利用扫描电镜、X射线衍射仪、X光能谱仪以及浆罐式冲蚀磨损试验机研究了2Cr13不锈钢表面激光熔覆Ni/50%Cr_3 C_2复合涂层的组织和冲蚀磨损性能Ni/50%Cr_3C_2激光熔覆层由细密的奥氏体枝晶和枝晶间的γ-M_7,C_3共晶体所组成,其显微硬度范围为350-450HV。在含有H_2SO_4和 NaCl的砂浆水溶液中且冲击角为 45°的情况下,冲蚀磨损率随冲击速度和酸性介质浓度的提高而增加,Ni/50%Cr_3C_2复合涂层冲蚀磨损表面形貌的典型特征为铲削坑和挤出唇。
The microstructure of stainless steel 2Cr13 laser cladding Ni / 50% Cr_3 C_2 composite coating properties and erosion Ni / 50 scanning electron microscope, X-ray diffraction, X-ray spectrometer and the plasma erosion and wear tester tank The% Cr_3C_2 laser cladding layer consists of γ-M_7, C_3 eutectic between fine dendrites and dendrites, and has a microhardness range of 350-450HV. In the case of mortars containing an aqueous solution of NaCl and H_2SO_4 and impact angle of 45 °, the erosion wear rate and improve the impact velocity with the acidic medium concentration increased, Ni / 50% Cr_3C_2 composite coating erosion surface morphology Typical features are shovels and extrusion lips.