【摘 要】
：
研究了在常压、通氧条件下 ,用浓硫酸浸取闪锌矿制取硫酸锌时酸浸条件对锌浸取率的影响。实验表明 ,当硫酸浓度为 40 % (质量比 ) ,液固比为 6～ 7∶1 (质量比 ) ,酸浸温度控制
【机 构】
：
湘潭工学院化学工程系!湘潭411201,湘潭工学院化学工程系!湘潭411201,中南工业大学化学化工学院!长沙410083
论文部分内容阅读
研究了在常压、通氧条件下 ,用浓硫酸浸取闪锌矿制取硫酸锌时酸浸条件对锌浸取率的影响。实验表明 ,当硫酸浓度为 40 % (质量比 ) ,液固比为 6～ 7∶1 (质量比 ) ,酸浸温度控制在 1 1 0～ 1 2 0℃ ,浸取时间为 2h ,氧流量为每升酸浸液 40～ 50cm3/min时 ,锌浸取率大于 95% ,闪锌矿中所含的硫大部分以单质硫析出。
The effect of acid leaching conditions on leaching rate of zinc was studied when zinc sulfate was obtained by leaching sphalerite from concentrated sulfuric acid at atmospheric pressure and oxygen. Experiments show that when the concentration of sulfuric acid is 40% (mass ratio), liquid-solid ratio is 6-7: 1 (mass ratio), the temperature of acid leaching is controlled at 110-120 ℃, the leaching time is 2h, For every liter acid leaching solution 40 ~ 50cm3 / min, the leaching rate of zinc is more than 95%, most of the sulfur contained in sphalerite is precipitated by elemental sulfur.
其他文献
Recent advances in information and communication technologies, such as mobile Internet and smartphones, have created new paradigms for participatory environment
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
对国内外综合管廊建设现状进行了分析、总结得出了国内综合管廊规划建设中存在的问题,并针对提出的问题给出了合理解决方法同时,对郑州市市民公文化服务区核心区综合管廊实例
研究了改性剂对季铵盐萃取分离钴 (Ⅱ )、铁 (Ⅱ )、锰 (Ⅱ )的影响。实验结果表明 ,有机酸HB改性剂在抑制钴 (Ⅱ )、铁 (Ⅱ )、锰 (Ⅱ )萃取的同时 ,改变了铁的萃合物的性质
采用多源磁控溅射物理气相沉积法在单晶硅片、20Cr和Cr12W表面制备了梯度变化非晶碳涂层,测试了非晶碳涂层的纳米硬度和弹性模量及摩擦磨损行为。结果表明:涂层具有较高的硬
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
郑州市提出“两环三十一放射”生态廊道快速路网体系 从生态廊道功能定位与横断面特征入手,分析主辅通道交通组织存在的问题,并结合郑州市生态廊道断面特征,提出交叉口处理方
对15个高产脂家系和思茅松种子园良种进行了遗传测定,结果表明:1年生思茅松种子园良种生长最好,树高、地径、冠幅分别超过对照56.9％、8.8％和31.3％,1年生高产脂家系苗高与对照相
本刊讯(张洪成报道)中国造纸学会第十五届学术年会于5月29日～31日在北京渔阳饭店召开,本届年会由中国造纸学会主办,中国制浆造纸研究院协办。来自全国的造纸行业及相关行业的