【摘 要】
：
The transformation behavior of precipitates in Al-Mg-Si-Cu alloys with and without Zn addition during artificial aging at 170℃ was investigated in this study.F
【机 构】
：
State Key Laboratory of Nonferrous Metals and Processes
【基金项目】
：
the National Key Research and Development Program of China(No.2016YFB0300802)。
论文部分内容阅读
The transformation behavior of precipitates in Al-Mg-Si-Cu alloys with and without Zn addition during artificial aging at 170℃ was investigated in this study.For Al-Mg-Si-Cu alloys with and without Zn addition,two types of precipitates,needle-like β“and lath-like L,are formed with the aging time increasing from 8 to 34 h.The needle-like β”precipitate exhibits a Mg-to-Si atomic ratio of 1.31 which is in agreement with the theoretical ratio of 1.25 for β“(Mg5Al2Si4).In addition,the β”precipitate is supposed to contain Al and Cu.With further partitioning of Mg,Si and Cu and release of Al,the needle-like β“pre-cipitate can transform to lath-like L phase.The L phase has significantly higher concentrations of Mg,Si and Cu and lower concentration of Al,with a higher Mg-to-Si atomic ratio(1.41)deviated from theoretical ratio of β”.However,the major of Zn has a random distribution in Al matrix and exhibits no significant partitioning into precipitates.Zn remained in matrix can enhance the transformation of β\"precipitates to L precipitates.
其他文献
The microstructure and corrosion resistance of Mg-0.5 Zn-0.2 Ca-0.2 Ce alloy with different processing conditions were investigated.The composition was detected by X-ray fluorescence(XRF),and the microstructure was analyzed by optical microscopy(OM)and sc
Zn-Fe and Y-modified Zn-Fe coatings were prepared on 42 CrMo steel through pack cementation processes at 370,390 and 410℃for 4 h.Y modification was achieved through the co-deposition of Zn and Y2 O3.The effects of Y modification on microstructure,formatio
The ADC12 aluminum alloy is prone to severe tool wear and high cutting heat during high-speed milling because of its high hardness.This study analyzes the highspeed milling process from the perspective of different chip morphologies.The influence of cutti
Inconel 625+WC composite coatings were prepared on the surface of 2Cr13 steel by laser cladding.The microstructure,microhardness and corrosion resistance of the composite coatings with different WC contents were investigated in detail.The results show tha
Mg alloy was protected with Mg:Al layered double hydroxide(LDH)coating intercalated with three green corrosion inhibitors(sodium benzoate,3-aminopropyltriethoxysilane and 8-hydroxyquinoline).The in-situ hydrothermal approach was adopted to intercalate cor
文中提出了粘贴聚丙烯膜作为PVDF压电薄膜的防热措施,运用单层板温升理论分析了防热效果。设计一种带有标准力传感器的摆锤装置,对有无粘贴聚丙烯膜的PVDF压电薄膜进行对比实验。结果表明:粘贴聚丙烯膜对PVDF压电薄膜动态灵敏度和响应特性均没有明显影响,是PVDF压电薄膜防热的有效措施。
为解决传统步进电机驱动器使用DSP芯片价格高和信号输入方式单一的问题,针对两相四线步进电机,使用ARM芯片设计了支持多种信号输入方式的步进电机驱动器,并开发了配套上位机。重点介绍了硬件电路设计和下位机程序设计,使用STM32F103C8T6芯片接收输入信号,将驱动器与控制器集成,同时支持串口、CAN和脉冲输入3种输入模式。实验结果表明:该驱动器满足多输入通信方式,运行稳定,成本低,适用于多种工业场合。
由于服役环境的复杂及流固耦合作用特征,运营中的海管会出现管道穿孔甚至断裂的问题,引发原油泄漏。因此,对海管结构变形进行监测,掌握结构的整体姿态,评价其结构安全性具有重要的工程意义。鉴于当前海管变形监测的光纤传感探头存在的缺陷,文中结合海管几何和物理特征,根据应变传递理论设计了一种适应输油气海管长期连续变形监测的硅橡胶封装光纤光栅传感器,并通过基础拉伸试验和模型试验检测其界面传递变形和应变感知性能,
为实现在低露点环境下的准确测量,应用α-Al2O3/SiO2电容传感器和露点标定技术,设计了具有温度补偿的电容式露点变送器。文中介绍了α-Al2O3/SiO2电容传感器的结构、传感器对微量水分响应的感湿机理以及变送器的硬件设计,并利用露点发生器和SDK-710快速高低温试验箱来模拟需要的实验环境,通过数据采集和数据处理,将露点温度、环境温度、频率值建立三维曲面关系,并用于软件
Sn/Ni-Sn/Sn sandwich joining piece was developed and applied to fabricate segmented half-Heusler/skutterudite thermoelectric joints,and high-temperature service behavior of the joints was studied.The microstructure and contact resistance of the joint befo