【摘 要】
：
Ta-W alloys have unique properties but their applications at high temperatures are restricted due to their poor oxidation resistances.The addition of Al and Ti
【机 构】
：
School of Materials Science and Engineering,North Minzu University,Yinchuan 750021,China;CNMC Ningxi
论文部分内容阅读
Ta-W alloys have unique properties but their applications at high temperatures are restricted due to their poor oxidation resistances.The addition of Al and Ti decreases the oxidation rate of the alloy,as Al-contained protective oxide layer could be formed.In this study,ternary and quaternary Ta-W alloys containing Al and Ti were prepared by hot press sintering.The microstructures and oxidation behaviors of the alloys were studied at 1173 K.The results show that the oxidation kinetics of all alloys follows a parabolic law at short oxidation periods.After cyclic oxidation,the kinetics of quaternary alloys still obeys the parabolic law but that of ternary alloy has been changed into linear law kinetics after 8-h oxidation.For ternary alloy,an outer layer with dense and continuous alumina was formed during the initial stage,and phase transformation caused the oxides to peel off.By compar-ison,the quaternary alloys depicted continuously solid solution of the oxides layer.Overall,Al and Ti played key roles in oxidation degree and affected the oxidation kinetics of ternary and quaternary alloys.
其他文献
Weight reduction plays an important role in reducing fuel and emissions,and the heat-treatable 6016 aluminum alloy exhibits excellent application prospect in automobile lightweight.In this paper,ingot with constant Mg/Si ratio and decreased Mg and Si cont
The metal-organic-decomposed lanthanum cerium oxide(LaCeO2)solution was spin-coated on p-type Si substrate to form thin films.The method of microwave-assisted annealing was adopted to modify the surface properties of the deposited thin films.Th
为了有效监测局部放电信号,利用FPGA的高速并行处理能力,设计一种基于FPGA的特高频局部放电监测硬件实现系统。文中介绍了系统的硬件设计及FPGA实现原理。系统使用提升小波变换对采集数据进行脉冲提取,然后对有效脉冲进行特征提取,最后将提取的特征参数送入PC端,使用DBSCAN将脉冲的特征提取结果进行聚类分离。实验结果表明,基于高速FPGA设计的局部放电监测硬件系统能将不同脉冲信号有效分离。
A novel phenomenon of spontaneous positive exchange bias(PEB)is reported in SrFeO3-x/SrCoO3-x epitaxial bilayer without undergoing any magnetic field treatment.When inserting a thick SrTiO3(STO)nonmagnetic spacer(about 6 nm)into the bilayer interface,this
The increase in zinc content in Al-Zn-Mg-Cu alloys provides an effective method to enhance the strength.Transmission electron microscopy(TEM)and tensile test were employed to analyze the microstructure and tensile properties,respectively,of Al-9.3 Zn-2.0
Rapid oxidation takes place both in the laboratory and in industrial conditions when alloy 925 is contaminated by oxide powder,and the oxidation rate is much higher than normal.Herein,the rapid oxidation behavior and mechanism of alloy 925 were investigat
The Ti51.44Zr16.26Cu30Sn2.3(at%)amorphous filler alloy in a ribbon form was prepared by melt spinning.The Ti-6 Al-4 V alloy was brazed in vacuum furnace by using the Ti51.44Zr16.26Cu30
Al2O3-ZrO2-TiO2 coatings were successfully prepared by plasma spraying Al2O3-ZrO2 composite powders with and without TiO2 addition.The effects of TiO2 on the ph
For the purpose of elevated temperature service and weight reduction in aerospace vehicle applications,a novel Ti-Zr-Fe-Cu-Ni-Co-Mo filler metal was employed to join TiAl to Ni-based superalloy(GH536).The effects of brazing temperature on interfacial micr
The magnesium alloy has a unique advantage in 3C fields due to its high specific strength and excellent electromagnetic shielding characteristic.However,it is d