采用自制的专用铁基合金粉末,对合金球墨铸铁风冷辊进行了激光熔覆修复。利用光学显微镜、X-射线衍射仪与数字显微硬度计对激光熔覆修复层的组织结构及硬度进行了研究。结果
【机 构】
：
方大特钢科技股份有限公司建安公司,南昌航空大学环境与化学工程学院,南昌航空大学材料科学与工程学院,
论文部分内容阅读
采用自制的专用铁基合金粉末,对合金球墨铸铁风冷辊进行了激光熔覆修复。利用光学显微镜、X-射线衍射仪与数字显微硬度计对激光熔覆修复层的组织结构及硬度进行了研究。结果表明,激光熔覆修复层呈树枝状晶生长,与风冷辊形成了良好的冶金结合,表面较平整、无气孔与裂纹,主要由过饱和马氏体与金属间化合物Fe3.5B组成,平均显微硬度达753 HV0.2,相对于风冷辊提高了约43.7%。
The homemade iron-based alloy powder is used to repair the alloy ductile iron wind-cooled roller by laser cladding. The microstructure and hardness of laser cladding layer were studied by optical microscope, X-ray diffraction and digital microhardness tester. The results show that the laser cladding layer has dendritic growth, which forms a good metallurgical bond with the air-cooled roller. The surface is smooth and free of pores and cracks. It mainly consists of supersaturated martensite and intermetallic Fe3.5B. The average microhardness reached 753 HV0.2, an increase of about 43.7% compared to the air-cooled roller.
其他文献
利用Gleeble-1500D热模拟试验机,对某厂A36船板钢的轧制工艺进行热模拟,通过单道次和双道次压缩试验,研究了A36钢热轧过程动态再结晶的临界应变量及静态软化行为,分析了终轧
通过MTS试验机、扫描电镜及能谱分析,对一种2100MPa级超高强度18Ni马氏体时效钢的恒应变低周疲劳破坏特性进行了研究。结果表明,时效时间对实验钢的低周应变疲劳性能的影响不
采用气压浸渗法实现了SiC/Al和SiO2构件的原位连接,SiC/Al复合材料组织浸渗致密,SiC颗粒的分布较均匀。该复合材料的主要断裂机制为基体和颗粒的混合断裂。SiC/Al和SiO2构件
用直接烧制法制备了竹炭(BC)材料,并采用恒流充放电、循环伏安(CV)和塔菲尔曲线研究了后期掺BC对LiFePO4/MWNTs电化学性能的影响.结果表明,后期掺杂5wt％BC时,所得LiFePO4/MWNT
通过粉末注射成形技术制备了SiC颗粒增强Cu基复合材料．并采用溶剂脱脂和热脱脂工艺对注射坯料进行脱脂，再对脱脂坯料进行了烧结，获得了致密烧结件。观察了不同SiC含量的SiCp／Cu复
以高能球磨法制备的WC与无定形Al2O3复合粉末为原料,研究烧结温度对WC-Al2O3复合材料组织和力学性能的影响,采用XRD和SEM对粉末及烧结试样的结构特征进行表征。结果表明:烧结
通过对V形90°形弯曲回弹的讨论,建立一个V形弯曲回弹测试模具。该项研究与设计,旨在能够事先不需要计算就可以掌握该材料的回弹性能。模具采用T形滑座与弯曲角两边的压板调
采用离子渗氮与多弧离子镀工艺相结合的复合处理方法,对齿轮材料复合处理的工艺进行研究与优化。实验证明,采用离子渗氮与多弧离子镀复合工艺,可以使过渡层与陶瓷涂层之间具
应用离子渗氮与多弧离子镀复合技术在40Cr基体上制备Ti1-xAlxN复合膜层,采用扫描电镜、XRD分析仪、显微硬度仪与划痕仪研究Al含量对膜层表面结构与性能的影响.结果表明:Al含
在铝酸盐体系溶液中对AZ91镁合金进行微弧氧化处理,用扫描电镜对所得不同厚度的微弧氧化膜层形貌进行观察;通过盐雾试验进行耐腐蚀性能测试;用X射线衍射仪进行膜层成分分析。