【摘 要】
：
Due to its high hardness,good red hardness and excellent wear resistance at high temperature,high speed steel(HSS)is fit for the roll manufacture.In order to ov
【机 构】
：
Xi′an Jiaotong University,Zhengzhou Institute of Aeronautics,
【出 处】
：
Journal of Iron and Steel Research(International)
论文部分内容阅读
Due to its high hardness,good red hardness and excellent wear resistance at high temperature,high speed steel(HSS)is fit for the roll manufacture.In order to overcome the segregation of centrifugal casting of HSS roll,die-cast processes were developed and its effects on the properties of the HSS roll were investigated.It was found that pressure,pressing time and speed are three important factors affecting shrinkage cavity.For pouring temperature of 1 400-1 450 ℃,pressure of 150-160 MPa,pressing time of 120-150 sand pressing speed of 14-16mm/s,a compact HSS roll was obtained,which has no segregation and small working allowance.In the high speed wire rod rolling mill,service life of the HSS roll is 5to 8times longer than that of high nickel chromium infinite chilled cast iron roll.
Due to its high hardness, good red hardness and excellent wear resistance at high temperature, high speed steel (HSS) is fit for the roll manufacture. Order to overcome the segregation of centrifugal casting of HSS roll, die-cast processes were developed and its effects on the properties of the HSS roll were investigated. It was found that pressure, pressing time and speed are three important factors affecting shrinkage cavity. For pouring temperature of 1 400-1 450 ° C, pressure of 150-160 MPa, pressing time of 120-150 sand pressing speed of 14-16mm / s, a compact HSS roll was obtained, which has no segregation and small working allowance.In the high speed wire rod rolling mill, service life of the HSS roll is 5to 8times longer than that of high nickel chromium infinite chilled cast iron roll.
其他文献
Interaction of antiworms with a worm population of e.g. hosts of worm infected and hosts of antiworm infected must be considered as a dynamic process. This stud
A new surfacing electrode is developed with cracking resistance and wearability based on high microhardness of TiC and VC, carbides of Ti and V are formed in de
Nickel-based catalyst [N,N]NiBr2, in which [N,N] stands for N-(2,6-diisopropylphenyl)pyridine-2-carboxaldimine, shows high activity for ethylene polymerization
The super high strength aluminum alloy ingots with 100 mm in diameter were cast by the process of low-frequency electromagnetic horizontal continuous casting (L
GP algorithm of correlation dimension computation is ameliorated which overcomes the shortage of traditional one. Improved process of GP algorithm takes the inf
The use of aluminum, particularly for engine blocks, has grown considerably in the past ten years, and continues to rise in the automotive industry. In order to
The half-wave potentials of disperse dyes with different structures are measured, the relationship between half-wave potentials and their discharge properties i
The spheroidiser is a necessary additive to manufacture ductile iron. Sometimes with the same hot metal,spheroidisers and treated technology, reactions differ g
In order to enforce the least privilege principle in the operating system, it is necessary for the process privilege to be effectively controlled; but this is v
The homogeneity of low alloy steels continuous casting billet obtained under different technological conditions has been investigated by original position stati