Lead halide perovskites have received increasing attention recently as a candidate material in various optoelectronic areas because of their high performance as light absorbers. Herein, we report the growth of CsPbI3 nanobelts via a solution process. A single-crystalline CsPbI3 nanobelt with uniform morphology can be achieved by controlling the amount of PbI2. A single-crystalline CsPbI3 nanobelt possesses a mean width, length, and thickness of 100 nm, 5 μm, and 20 nm, respectively. In this work, photodetectors (PDs) based on individual CsPbI3 nano-belts are constructed and found to perform well with an external quantum efficiency and responsivity of 2.39 × 105％ and 770 A/W, respect-ively. The PDs also show a high detectivity of up to 3.12 × 1012 Jones, which is at par with that of Si PDs. The PDs developed in this work ex-hibit great promise in various optoelectronic nanodevices.