The microstructure and mechanical properties of cast inserted dies for automobile covering components were studied. The results show that the as-cast microstructures of cast inserted dies are composed of pearlite, martensite, bainite, and austenite; and that the annealed microstructure is granular pearlite. The mechanical properties of cast inserted dies approach that of forged inserted dies. The tensile strength is 855 MPa, the elongation is 16%, the impact toughness is 177 J/cm2, and the hardness after annealing and quenching are HRC 19 and HRC 60-62. In addition, the cast inserted dies have good hardenability. The depth of the hardening zone and the hardness after flame quenching satisfy the operating requirements. The cast inserted dies could completely replace the forged inserted dies for making the dies of automobile covering components.
The microstructure and mechanical properties of cast inserted dies for automobile covering components were studied. The results show that the as-cast microstructures of cast embedded dies are composed of pearlite, martensite, bainite, and austenite; and that the annealed microstructure is granular pearlite. The mechanical properties of cast inserted dies approach that forged inserted dies. The tensile strength is 855 MPa, the elongation is 16%, the impact toughness is 177 J / cm2, and the hardness after annealing and quenching are HRC 19 and HRC 60- The depth of the hardening zone and the hardness after flame quenching satisfy the operating requirements. The cast of the dies could completely replace the forged inserted dies for making the dies of automobile covering components.