【摘 要】
：
The approximately equimolar ratio AlCrNiSiTi multi-principal element alloy (MPEA) coatings were fabricated by laser cladding on Ti-6Al-4V (Ti64) alloy.Scanning
【机 构】
：
School of Materials Science and Engineering, Chongqing University of Technology, Chongqing 400054, C
论文部分内容阅读
The approximately equimolar ratio AlCrNiSiTi multi-principal element alloy (MPEA) coatings were fabricated by laser cladding on Ti-6Al-4V (Ti64) alloy.Scanning electron microscopy (SEM),equipped with an energy-dispersive spectroscopy (EDS),and X-ray diffraction (XRD) were used to characterize the microstructure and composition.Investigations show that the coatings consist of (Ti,Cr)5Si3 and NiAl phases,formed by in situ reaction.The phase composition is initially explicated according to obtainable binary and tary phase diagrams,and the formation Gibbs energy of TisSi3,VsSi3 and CrsSi3.Dry sliding reciprocating friction and wear tests of the AlCrNiSiTi coating and Ti64 alloy substrate without coating were evaluated.A surface mapping profiler was used to evaluate the wear volume.The w surface was characterized by SEM-EDS.The hardness and wear resistance of the AlCrNiSiTi coating are well compared with that of the basal material (Ti64).The main wear mechanism of the AlCrNiSiTi coating is slightly adhesive transfer from GCr15 counterpart,and a mixed layer composed of transferred materials and oxide is formed.
其他文献
分析了制备工艺过程、球磨设备、试样放置时间以及球磨时间对NaAlH4放氢性能的影响.其中除了试样3是采用高能球磨机外,其它所有试样均采用行星式球磨机.结果表明,这些因素对N
A phenomenological crystal plasticity constitutive model for magnesium single crystal was presented.Four deformation mechanisms(including basal〈a〉,prismatic〈
采用Gleeble-3500热模拟试验机对一种新型的耐热高强度铝合金211Z.X进行等温压缩试验,研究其热变形行为,试验条件为温度350~500℃、应变速率0.01~10.00 s~(-1)。试验得出了该
2006~2007年在棉花结铃盛期,从新疆奎屯和石河子等地的不同棉田中采集细菌性烂铃病样,分别从病部棉绒、种子和铃壳上分离纯化得到了20个细菌菌株;使用针刺法接种棉铃后,所有
【摘要】云计算是高职院校实训教学过程中的重要组成部分。云计算能够满足高职院校实训教学过程中的设备使用要求，提高实训教学质量。本文对云计算环境下的高职院校实训教学进行分析，为学生营造一个良好的学习氛围。 【关键词】云计算 高职院校 实训教学 教育理念 【中图分类号】G712【文献标识码】A 【文章编号】2095-3089（2016）05-0020-02 1.前言 教育理念的革新，使高职院校逐
Active control of turbine blade tip clearance for aircraft engine continues to be a conc in engine operation,because turbine blades are subjected to wear and th
利用循环伏安法、计时电势法和计时电流等方法,研究了钨在700℃的NaCl-KCl-NaF-Na2WO4熔盐中的电化学反应机理和电结晶过程.结果表明,钨的电化学反应过程为由离子扩散速率和
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
通过研究C微合金化对层片组织Ti Al合金800℃/300 MPa蠕变变形行为、组织分解以及应变硬化的影响,以解释C微合金化对层片组织高应力蠕变变形均匀性的影响。结果表明:在Ti-47.
采用扫描电镜、扫描透射电镜、透射电镜等分析手段,对银氧化铜复合材料中氧化铜颗粒的结构进行了分析.结果表明,可变形氧化铜的晶体结构为立方结构,其变形量最大可达300％;不变