采用扫描电镜、光学显微镜、X射线衍射仪等研究了在535℃下不同固溶时间对金属型铸造和粉末触变成形6061铝合金组织的影响。结果表明,粉末触变成形6061铝合金在535℃固溶处理
【机 构】
：
兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室,兰州理工大学有色金属合金教育部重点实验室,
论文部分内容阅读
采用扫描电镜、光学显微镜、X射线衍射仪等研究了在535℃下不同固溶时间对金属型铸造和粉末触变成形6061铝合金组织的影响。结果表明,粉末触变成形6061铝合金在535℃固溶处理3h后,共晶相充分固溶到α-Al基体内部,初生相颗粒与二次凝固区的颗粒通过合并长大。而金属型铸造6061铝合金经过6h固溶处理后,共晶相固溶完毕,与粉末触变成形相比,金属型铸造的固溶进程较慢。
The effects of different solid solution time on the shape and the thixoforming of 6061 aluminum alloy were investigated by scanning electron microscopy, optical microscope and X-ray diffraction. The results show that the eutectic phase of 6061 aluminum alloy is solid-solutioned to α-Al matrix after solution treatment at 535 ℃ for 3h. The particles of primary phase and secondary solidification zone grow up by combining. After 6h solution treatment, the solid solution of eutectic phase of 6061 aluminum alloy is completed. Compared with the thixoforming, the solid solution process of metal casting is slower.
其他文献
采用高能超声振动制备Mg-6Zn-3RE-1.4Y镁合金的半固态浆料,并进行流变挤压铸造。研究了挤压压力对该镁合金组织及力学性能的影响。结果表明,随着流变挤压压力由0增大到200 MP
采用放电等离子烧结(SPS)工艺在950℃、40 MPa下烧结20 min后随炉冷却,制得Cu-50Mo触头合金材料.测试结果表明,显微硬度(HV)、电导率和致密度分别达到116、21.5 MS/m和92.5%,
目的 评价吸人高低氧联合后程加速超分割放疗对食管癌的临床疗效.方法 74例患者随机分为试验组和对照组.试验组常规分割放疗DT 38～40 Gy后改为DT 1.3～1.4 Gy/次,每天2次,间隔时间＞6 h,中位总剂量DT 64.2 Gy,放疗过程中先后吸入高低浓度氧.对照组常规分割放疗1.8～2.0 Gy/次,每周5次,中位总剂量65.6 Gy.结果 获得病例71例.放疗DT30 cy时,试验组
数值模拟了镁合金铸轧凝固中传热与流动过程,分析了铸轧速度对铸坯凝固温度场、流场的影响。制备了镁合金铸轧板坯,采用金相显微镜、扫描电镜等分析了板坯组织、形貌及成分分
对7075铝合金单道次等通道转角挤压过程进行了正交试验研究,并进行了微观组织观察。试验结果表明,90°转角挤压后试样的晶粒细化效果最好。基于Zener-Hollomon参数模型,在设
利用Gleeble-1500热模拟试验机对均匀化7050铝合金在573~723℃和0.000 5~1s-1变形条件下进行热压缩试验。通过线性回归分析计算出均匀化7050铝合金的应变硬化指数以及变形激
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
采用电弧喷涂技术在石膏表面制备Zn-Cu合金涂层,利用正交试验研究了喷涂工艺参数对涂层硬度、孔隙率和磨损量的影响。结果表明,在研究范围内,影响涂层硬度最主要的参数为喷涂
通过配制铁基金属粉末,利用激光熔覆技术,对45号钢进行表面改性。利用XRD、TEM、电化学工作站与盐雾试验研究了熔覆层的组织和耐蚀性能。研究表明,获得的铁基金属粉末适合45
目的探讨腹腔镜干下子宫肌瘤剔除术的临床应用价值。方法子宫肌瘤70例随机分为腹腔镜干下子宫肌瘤剔除手术组40例,开腹子宫肌瘤剔除术组30例,对两组的手术时间、术中出血量、