Ultra-high vacuum gaseous hydrogen permeation experiments on Fe3Al-based alloy were performed in the temperature range of 330 ~450℃ with an upstream hydrogen pressure between 3.38 × 104 Pa and 7.28 × 104 Pa. The results show that the hydrogen diffusivity and permeability in Fe3Al-based alloy obey Arrhenius relationship in the experimental temperature range and the hydrogen permeation process is controlled by the lattice diffusion of hydrogen at relative high temperature. The activation energy of hydrogen diffusion in the Fe3Albased alloy was found to be 75 kJ/mol.