The effects on abrasion resistance and the microstructure of GCr15 steel surface by the compound technology of permeating RE combined with laser melting modification was studied. The results show that after compound treatment, the abrasion resistance of samples has been improved significantly and the weight loss has been reduced to 14% of blank sample; the microstructure has been denser and more uniform than that of untreated; meanwhile, the grain has been refined and the concentration gradients of the elements permeated have been decreased obviously.