对集装箱板在轧制过程中出现的翘皮问题进行电镜扫描及能谱分析,认为翘皮的产生是由于冶炼时保护渣未处理干净,同时由于加热或轧制时局部高温,产生氧化,在较浅的表面区域形成氧化物,当夹杂物较多且体积较大时,由于夹杂物距离表面较浅,经过多道次轧制后夹杂物从表面溢出,从而带动附近金属撕裂形成翘皮。 During the rolling of the container plate, the problem of the warpage was observed by scanning electron microscope and energy spectrum analysis. The result showed that the warpage occurred due to the unprocessed clean slag during the rolling process and the oxidation due to the local high temperature during heating or rolling. The shallow surface area forms oxide. When there are more inclusions and larger volume, the inclusions will overflow from the surface after multi-pass rolling as the inclusions are shallow from the surface, tearing the nearby metal to form a warp .