The intermetallic compound Zr1-xTixCo was prepared and its suitability for hydrogen storage was investigated. The alloys obtained by magnetic levitation melting with the composition of Zr1-xTixCo (x=0, 0.1, 0.2 and 0.3, at.%) show single cubic phase by X-ray diffraction. A single sloping plateau was observed on each isothermal, and pressure-composition-temperature (PCT) measurement results show that the equilibrium hydrogen desorption pressure of Zr1-xTixCo alloy increases with increasing Ti content. The desorption temperatures for supplying 100 kPa hydrogen are about 665, 642, 621 and 614 K for ZrCo, Zr0.9Ti0.1Co, Zr0.8Ti0.2Co and Zr0.7Ti0.3Co alloy, respectively. Repeated hydrogen absorption and desorption cycles do not generate separated ZrCo, TiCo and ZrH2 phases, indicating that alloys have good thermal and hydrogen stabilization.
The intermetallic compound Zr1-xTixCo was prepared and its suitability for hydrogen storage was investigated. The alloys obtained by magnetic levitation melting with the composition of Zr1-xTixCo (x = 0, 0.1, 0.2 and 0.3, at.%) Show single cubic phase by X-ray diffraction. A single sloping plateau was observed on each isothermal, and pressure-composition-temperature (PCT) measurement results show that the equilibrium hydrogen desorption pressure of Zr1-xTixCo alloy increases with increasing Ti content. The desorption temperatures for supplying 100 kPa hydrogen are about 665, 642, 621 and 614 K for ZrCo, Zr0.9Ti0.1Co, Zr0.8Ti0.2Co and Zr0.7Ti0.3Co alloy, respectively. Repeated hydrogen absorption and desorption cycles do not generate separated ZrCo, TiCo and ZrH2 phases, indicating that alloys have good thermal and hydrogen stabilization.