采用高温固相法制备ZnO∶Zn绿色发光粉体。XRD分析、荧光光谱分析结果表明 :在固相法制备ZnO∶Zn中 ,制备原料所用ZnO、C的最佳摩尔比在 2∶3,反应最佳温度为 110 0 0C。
High-temperature solid-state preparation of ZnO: Zn green luminescent powder. The results of XRD and fluorescence spectroscopy showed that the best molar ratio of ZnO and C was 2: 3 and the best reaction temperature was 110 0 0C in ZnO:Zn prepared by solid state reaction.