The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal. The formation phase and interface structure of the joints were investigated by electron probe microanalysis (EPMA), scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the joint strength was tested by shearing method. The results showed: there occurred three new formation phases, Cu(s.s), FeNi and Ag(s.s) in TiC cermet/iron joint. The interface structure was expressed as TiC cermet/Cu(s.s)+FeNi/Ag(s.s)+a little Cu(s.s)+a little FeNi/Cu(s.s)+FeNi/iron, With brazing time increasing, there appeared highest shear strength of the joints, the value of which was up to 252.2MPa when brazing time was 10min.
The brazing of TiC cermet to iron was carried out at 1223K for 5-20 min using Ag-Cu-Zn filler metal. The formation phase and interface structure of the joints were investigated by electron probe microanalysis (EPMA), scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the joint strength was tested by shearing method. The results showed: There are three new formation phases, Cu (ss), FeNi and Ag (ss) in TiC cermet / iron joint. The interface structure was expressed as TiC cermet / Cu (ss) + FeNi / Ag (ss) + a little Cu (ss) + a little FeNi / Cu (ss) + FeNi / iron, with brazing time increasing, the joints, the value of which was up to 252.2 MPa when brazing time was 10 min.