论文部分内容阅读
New Mg2Si based Alloy for Automobile Engine Cylinder Liner
【机 构】
：
School of Transportation and Automotive Engineering,Xihua University,Chengdu,610039,China;Sichuan Su
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
【发表日期】
：
2011年4期
其他文献
In-situ magnesia-rich spinel fiber was formed resulting from the addition of ferro-cene into MgO-C refractory matrixes.The formation of in-situ spinel fiber was detected to start at 1300 ℃.The amount,diameter and length of the fibers increased with rising
Surface Modification of Silk Fibroin Films with Zwitterionic Phosphobetaine to Improve the Hemocompa
The experimental creep data were focused on wood-flour(WF)/poly vinyl chloride (PVC)composites with the variations in additive concentrations of wood flour,silane coupling agent, organomodified montmorillonite(OMMT)and nano-cacium carbonate(nano-CaCO_3).T
Performance of CTBN(carboxyl-terminated poly (butadiene-co-acrylonitrile))-EP(diglycidyl ether of bi
CTBN-EP prepolymers were synthesized from CTBN and epoxy resin under the catalysis of HTMAB.FTIR analyses indicate the formation of ester group between the carboxyl group of CTBN and the oxirane group of epoxy resin.The viscosity of modified prepolymer in
Influence of Water Content on Conductivity and Piezoresistivity of Cement-based Material with both C
Temperature Effect on the Photocatalytic Degradation of Methyl Orange under UV-vis Light Irradiation
Flame-retardant mechanism of magnesium oxychloride (MOC) in EP was in-vestigated by limiting oxygen index (LOI), XRD, SEM, TG-DTG and DSC. The results show that MOC performed well as an inorganic flame-retardant in EP. When the content of MOC is 50%, the
Detecting Impact Damage in Carbon Fabric/epoxy-matrix Composites by Ultrasonic F-scan and Electrical
Fe_(68)Zr_(20)B_(12) amorphous alloy was prepared by mechanical alloying(MA)method and annealed at different temperatures.Microstructures and magnetic properties of Fe_(68)Zr_(20)B_(12) alloys as-milled and annealed at 693,843,943 and 993 K were studied.T
SiC/Cu composites were prepared by hot pressing.The high temperature tribological properties of the composites were investigated.XRD,SEM techniques were carried out to characterize the samples.It is found that the friction coefficient of SiC/Cu composites