Preparation and sintering properties of zirconia-mullite-corundum composites using fly ash and zirco

来源 :中国有色金属学报 | 被引量 : 0次 | 上传用户:Q13696800
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Zirconia-mullite-corundum composites were successfully prepared from fly ash, zircon and alumina powder by a reaction sintering process. The phase and microstructure evolutions of the composite synthesized at desired temperatures of 1 400, 1 500 and 1 600 ℃ for 4 h were characterized by X-ray diffractometry and scanning electronic microscopy, respectively. The influences of sintering temperature on shrinkage ratio, apparent porosity and bulk density of the synthesized composite were investigated. The formation process of the composites was discussed in detail. The results show that the zirconia-mullite-corundum composites with good sintering properties can be prepared at 1 600 ℃ for 4 h. Zirconia particles can be homogeneously distributed in mullite matrix, and the zirconia particles are around 5 μm. The formation process of zirconia-mullite-corundum composites consists of decomposition of zircon and mullitization process.
其他文献
The influencing factors of surface alloying layer by evaporative pattern casting technology were investigated. A certain thickness alloying layer was formed on
The general behavior of micron-particles in the inner domain of porous ceramic vessel was simulated by computational fluid dynamics software in terms of samplin
Microstructural evolution and the relationship between microstructure and property during heat treatments in a new NiAl-based alloy (Ni-26.6Al-13.4Cr-8.1Co-4.3T
The phase evolution in (88%-91%)Mg-8%Sn-l%Zn-X (X=A1, Mn and/or Ce) system was analyzed via CALPHAD method and simulations were used in precise selection of the
Reactive mechanical alloying (RMA) was carried out in a planetary ball mill for the synthesis of ternary hydride Mg2FeH6 for hydrogen storage. The formation mec
Zn2+- TiO2 nanotube arrays were prepared by anodic oxidation method. The current-time curves were used to investigate their growth mechanism. Scanning electron
Three-dimensional (3D) flower-like anatase TiO2 nanostructures and flower-like titanate nanostructures were successfully synthesized via hydrothermal synthesis
The effects of precipitates on the fatigue crack growth rate of AA 7055 Al alloy subjected to different ageing treatments were investigated using transmission e
A simple electrochemical method for the in situ preparation of homogeneously dispersed gold-polyaniline core/shell nanocomposite particles with controlled size
Nd-F species in NdF3-LiF melts were studied using cryoscopic method. Liquidus temperatures of melts of various compositions were determined by differential ther