近日,攀钢研究院在鞍钢开展了2017年首轮TA2纯钛中厚板热轧试验,并取得圆满成功。过去轧制的厚薄规格板坯,由于加热出炉的坯料温度不均导致镰刀弯等板型缺陷,后期表面处理要增加工序,产品成本居高不下。针对上述问题,攀钢研究院科研人员开展了大量的基础性研究工作,制定了一系列改善和提高产品质量的工艺措施。试验结果表明,通过轧制工艺的优化和改进,成功解决了轧制薄规格板
Recently, Panzhihua Iron and Steel Research Institute in Angang carried out the first round of 2017 TA2 pure titanium plate hot-rolled test, and achieved complete success. The thickness of the past specifications of the rolling slab, as a result of uneven heating of the blank temperature caused sickle bend plate defects, post-surface treatment to increase the process, high product costs. In response to the above problems, Panzhihua Iron and Steel Research Institute researchers carried out a large number of basic research work, developed a series of process measures to improve and improve product quality. The test results show that, through the optimization and improvement of the rolling process, the successful solution to the rolling thin gauge plate