Mg-1.5Zn-0.2Zr-xCe (x=0, 0.1, 0.3, 0.5, mass fraction, %) alloys were prepared by conventional semi-continuous casting. The effect of rare earth Ce on the micro
The effect of step-quenching on the microstructure of aluminum alloy 7055 after artificial aging was studied by hardness testing and transmission electron micro
The dynamic recrystallization refinement of magnesium alloy AZ80 by compression tests was studied, and its effect on the mechanical properties was investigated.
An Al2O3 protective coating on magnesium alloy AZ31 was prepared by a repeated direct sol-gel process annealing at 300 ℃ and a composite coating was also depos
Dissimilar friction stir welding between 5052 Al alloy and AZ31 Mg alloy with the plate thickness of 6 mm was investigated. Sound weld was obtained at rotation
Both Mg-1Mn-3.5Y and Mg-1Mn-1Y-2.5Nd alloys (mass fraction, %) were extruded at 380 ℃. Most of the (10(1)0) crystal planes in the Mg-1Mn-3.5Y alloy are paralle