研究了硫化时间对氯丁橡胶4172混炼胶物理机械性能、耐热性能及高温耐老化性能的影响。结果表明,延长硫化时间可使混炼胶的硬度、拉伸性能、起始降解温度及降解过程中的焓变
论文部分内容阅读
研究了硫化时间对氯丁橡胶4172混炼胶物理机械性能、耐热性能及高温耐老化性能的影响。结果表明,延长硫化时间可使混炼胶的硬度、拉伸性能、起始降解温度及降解过程中的焓变逐步降低,压缩永久变形增大,但变化幅度都不大。通过DSC测试了混炼胶热焓变化值,并推导出了高温老化速率方程。延长硫化时间可使混炼胶在120℃下老化速度加快。
The effects of curing time on physical and mechanical properties, heat resistance and high temperature aging resistance of neoprene 4172 were studied. The results showed that the hardness, tensile properties, initial degradation temperature and enthalpy change of the mixture decreased gradually and the compression set increased with the extension of the curing time, but the variation range was not large. The change of enthalpy of the mixture was measured by DSC, and the equation of high temperature aging rate was deduced. Extend the curing time can make the rubber mix at 120 ℃ aging speed.
其他文献
The bilayer compounds[n-CnH2n+1N(CH3)3]2Zn Cl4(n=16,18)experience solid-solid phase transition within the temperature range of 310 to 340 K.The low-temperature
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
目的研究肠吉泰对肠易激综合征(irritable bowel syndrome,IBS)内脏敏感大鼠脊髓背根神经节5-羟色胺2A受体(5-HT_(2A) receptor,5-HT_(2A)R)、5-羟色胺7受体(5-HT_7receptor,
In this study, a series of imidazolium salts with different N3-substituents(3-position: methyl, vinyl, ethyl, n-propyl, n-butyl)-based ionic-liquid crystals wit
经过一年多努力,几经数稿,由深圳交响乐团创作的新作《大提琴与乐队/英雄独白——献给抗日女杰赵一曼》八月定稿并录制。作品总体构思、主旋律由“深交”老团长、大提琴家姜
目的分析和探讨老年癌症患者的生存质量及影响因素。方法对福州市鼓楼区116例老年癌症患者的生存状况进行流行病学调查；采用因子分析、逐步回归分析和典型相关分析方法对调查结果进行分析。结果与描述生存质量的典型变量V有较大相关系数的变量为：年龄、职业、生存时间、手术、化疗、中草药、家庭护理条件。结论老年癌症患者的生存质量主要受上述因素的影响，改善老年人的心理状态及增加其社会交往能力，有利于癌症患者的康复。
采用实时红外光谱仪(RT-FTIR)研究了单体结构、单体配比以及活性稀释剂结构对樟脑醌(CQ)/胡椒环(BDO)引发的光聚合动力学的影响,结果发现,UDMA虽然黏度较低,但是易发生链转移
社会音乐教育是国家整个音乐教育中的一个重要组成部分。因其办学方式多样,普及面广,教学方式灵活,在很大程度上契合了现代家庭的需求。在学习型社会背景下,社会音乐教育出现