【摘 要】
：
The influence of zirconium on the resistance to high temperature softening of 6082 Al-Mg-Si alloys has been researched. The softening process of 6082 alloys wit
【机 构】
：
Material Science Department,Shanghai Huizhong Automotive Manufacturing Co.
论文部分内容阅读
The influence of zirconium on the resistance to high temperature softening of 6082 Al-Mg-Si alloys has been researched. The softening process of 6082 alloys with Zr and without Zr, isothermally conditioned at 250℃, has been investigated. The results show the inclusion of Zr inhibits the decrease of HB in hardness(HB) compared with the alloys without Zr. This is due to the Zr and Al forming coherent dispersoid-Al3Zr, and Al3Zr particles within an Al matrix, which effectively restricts grain boundary movement. A study is also carried out to investigate the changes in resistivity, which occurs during the ageing of alloys containing Zr, compared to those without Zr. It is found that in both cases there is an initial rapid rise in resistivity followed by a slower rise in resistivity as ageing proceeds. The value of resistivity is lower for6082 alloys with Zr compared with 6082 alloys without Zr; this is explained in terms of the role of Zr in the 6082 alloys.
其他文献
为了研究SiCw·SiCp/2024Al复合材料的热变形行为,对压铸法制备的SiCw·SiCp/2024Al复合材料进行了热挤压变形,并测定了其变形前后的室温拉伸性能.利用扫描电镜和透射电镜对
Closed Field Unbalanced Magnetron Sputter Ion Plating (CFUBMSIP) systems have been used increasingly for PVD coating in recent years. TiN and CrN coatings, comm
In the present work, attempts have been made to extend the use of the tribological and chemical properties of rutile-TiO2 to metallic alloy systems, by forming
A bath of electroless plating Ni on the AZ91D magnesium alloy, containing sulfate nickel, was given in this paper. The nucleation mechanism of Ni-P deposits on
This paper gives a short introduction to the typical process route and material properties of these steels in comparison to standard martensitic corrosion-resis
A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath
Amorphous gels were processed with a varying Fe/Ba ratio of 11/5, 28/2, 10.5/1 in water and Solvent. Iron and barium nitrites with specific molar ratio was solv
The present work has investigated the effect of trace elements Cd and Sn on the microstructure and mechanical properties of Al-Si-Cu-Mg cast alloy. With the inc
In the present reserch, a model has been proposed for estimate fracture toughness of Nickel-phosphorus (EN) layers. For this purpose, high phosphorus (9%) EN co
Nowadays, in the auto industry, the need for improvement of fuel efficiency is getting increased more and more in terms of the global warming, as well as the ne