【摘 要】
：
Ceria-zirconia solid solution has been prepared by the urea grind combustion and citric acid sol-gel methods for catalytic applications as oxygen storage/release materials in this study.The properties and oxygen storage/release capacities of samples with
【机 构】
：
Key Laboratory of Coal Science and Technology, Taiyuan University of Technology, Ministry of Educati
论文部分内容阅读
Ceria-zirconia solid solution has been prepared by the urea grind combustion and citric acid sol-gel methods for catalytic applications as oxygen storage/release materials in this study.The properties and oxygen storage/release capacities of samples with different Zr contents were characterized and evaluated by X-ray diffraction (XRD),N2 adsorption,scanning electron microscopy (SEM),Raman spectroscopy,and insitu CO-CO2 looping test.The results demonstrate that the samples prepared by two methods are all of excellent lattice [O] release/storage properties and maintain good long-term cycle stability.But the preparation method significantly impacts the homogeneity of samples related to their redox properties and the content of Zr over 20％,which greatly changed the properties of ceria-zirconia solid solutions and caused their changing of crystalline symmetry from cubic to tetragonal.The samples prepared by citric acid solgel method are of more homogeneous particle sizes and higher specific surface areas than that by urea grind combustion method,which is benefit to the oxygen release rather than oxygen storage.The bulk oxygen amount migrated to surface increases with the increasing Zr content,however,the amount of lattice oxygen migration decreases when Zr content is over 20％.When Zr content is 20％,the differences of storage/release capacities from two different preparation methods are reduced at high temperature in the long-term loop reaction.
其他文献
One of the major challenges associated with fuel cells is the design of highly efficient electrocatalysts to reduce the high overpotential of the oxygen reduction reaction (ORR).Here we report Polyaniline (PANI) based micro/nanomaterials with or without t
Organometal halide perovskite based solar cells have emerged as one of the most promising candidates for low-cost and high-efficiency solar cell technologies.Here a Vapor Transfer Method (VTM) is used to fabricate high quality perovskite thin films in a b
2D nanosheets such as graphene,silicene,phosphorene,metal dichalcogenides and MXenes are emerging and promising for lithium storage due to their ultrathin nature and corresponding chemical/physical properties.However,the serious restacking and aggregation
Lithium sulfide (Li2S) provides a promising route for lithium storage due to high theoretical specific capacity (1166 mAh g-1).The electrochemical performance of Li2S can be significantly enhanced by forming Li2S-carbon composites with the introduction of
Development of efficient and promising bifunctional electrocatalysts for oxygen reduction and evolution reactions is desirable.Herein,cobalt nanoparticles embedded in nitrogen and sulfur co-doped carbon nanotubes (Co@NSCNT) were prepared by a facile pyrol
Wormholelike mesoporous carbons (WMCs) with three different pore diameters (Dp),namely WMC-F7 (Dp =8.5 nm),WMC-F30 (Dp=4.4nm),and WMC-F0 (Dp=3.1 nm) are prepared via a modified sol-gel process.Then PtRu nanoparticles with the panicle size (dpt) of ～3.2 nm
Ni-based anodes of SOFCs are susceptible to coking,which greatly limits practical application of direct methane-based fuels.An indirect internal reformer is an effective way to convert methane-based fuels into syngas before they reach anode.In this work,c
A sustainable strategy for Fischer-Tropsch iron catalysts is successfully achieved by embedding of synergistic promoters from a renewable resource,corncob.The iron-based catalysts,named as “corncob-driven”catalysts,are composed of iron species supported o
Calcium hydroxyapatite (HAp) supported cobalt and cobalt-cerium catalysts were examined for hydrogen production in glycerol steam reforming.The catalysts were synthesized by incipient wetness impregnation method and characterized through X-ray diffraction
X1 (MeO-TPD) is an inexpensive and easily synthesized π-conjugated molecule that has been used as a hole-transport material (HTM) in solid-state dye-sensitized solar cells (ssDSSCs),achieving relatively high efficiency.In this paper,we characterize the ph