Several alloying elements involving Zr, Cu, Zn and Sc were added to Al-Mg sheet alloys in order to obtain an excellent combination of high strength and good high-temperature formability. Microstruc-tural examination showed that coarse intermetallic particles were formed in the microstructure and their amounts changed with variations of the alloying elements. During warm rolling of thermome-chanical treatments prior to warm deformation, the coarse particles initiated cracks, decreasing the warm formability. For healing the crack damage and further improving the warm formability, a process of hot isothermal press was developed and optimized to the sheet alloys. With this process, the biaxial stretch formability at 350℃ was improved by 22% for an aluminum alloy containing a large amount of coarse particles.
Several alloying elements involving Zr, Cu, Zn and Sc were added to Al-Mg sheet alloys in order to obtain an excellent combination of high strength and good high-temperature formability. Microstruc-tural examination showed that coarse intermetallic particles were formed in the microstructure and their amounts changed with variations of the alloying elements. During warm rolling of thermome-chanical treatments prior to warm deformation, the coarse particles prepared cracks, decreasing the warm formability. With this process, the biaxial stretch formability at 350 ° C was improved by 22% for an aluminum alloy containing a large amount of coarse particles.