【摘 要】
：
Dy-Fe alloy replace dysprosium in the NdFeB permanent material can improve the performance and productivity and cut the cost.The electrolyte is a binary system
【机 构】
：
Research Institute for Rare Earth Application Technological,Baotou Huali Rare Earth Co. Ltd.
论文部分内容阅读
Dy-Fe alloy replace dysprosium in the NdFeB permanent material can improve the performance and productivity and cut the cost.The electrolyte is a binary system of molten DyF3-LiF.Iron is cathode and graphite is anode.The raw material is Dy2O3 oxide.The content of dysprosium is (78 ～85 ) ± 1% in the Dy-Fe alloy made by electrolyzing in the industry producing.In the course of electrolyzing the efficiency of current, the alloy formation and the productivity of rare earths by studying the formation of electrolyte, the electrolyzing temperature, the standards and the current density of cathode, the anode shape etc were studied.The conclusion is that we can produce Dy-Fe alloy (the content of dysprosium is (78 ～ 85 ) ± 1% ) in this condition, the efficiency of current is greater than 68 %, and the productivity of rare earth is greater than 92%.The content of oxygen, calcium, wolfram is smaller than the content by reducing.
其他文献
The influences of category and density of reagents, temperature and the value of pH in the solution of stripping the nickel coating on NdFeB permanent magnet on
The recoveries of phosphorus and RE of ore from Zhijin in Guizhou were studied.The influences of the calcination temperature, resident time, the digested time a
BaTiO3 ceramics doped with various quantities of Nd2O3, Sm2O3, Gd2O3, Dy2O3 and Er2O3 were prepared respectively ( the adulterate concentrations were 0. 001,0.
The abnormal growth of grains of sintering Nd13.6 Dy0.4 Fe79.5 B6.5 magnets were investigated in low oxygen manufacturing process.The abnormal growth of grains
Magnetic refrigeration techniques based on the magnetocaloric effect (MCE) were demonstrated as a promising alternative to conventional vapour-cycle refrigerati
Based on the analysis of flow characteristics of the FCC riser feedstock injection zone, two novel feedstock injection structures are put forward. By investigat
Based on a nonlinear state predictor (NSP) and a strong tracking filter (STF), a sensor fault tolerant generic model control (FTGMC) approach for a class of non
The investigations on the ferroelectric and dielectric properties of neodymium-doped Bi4Ti3O12 (Bi4-xNdxTi3 O12 ) ferroelectric ceramics were presented. The fer
The RE and composition of trace elements analysis show that phosphorite-ores are rich in ∑ RE concentration generally in Xinhua, Zhijin.The phosphorites were m
The synthesis of carbon nanotubes (CNTs) from methane decomposition by Ni-La-Al (Ni/La/Al = 10: 1:9) and Ni-Al (Ni/A1 = 1:1 ) catalysts at 1023 K was studied.Ca