【摘 要】
：
Novel Er3+-doped bismuth lead strontiam glass was fabricated and characterized, and the absorption spectrum and upconversion spectrum of the glass were studied.
【机 构】
：
Shanghai Institute of Optics and Fine Mechanics
论文部分内容阅读
Novel Er3+-doped bismuth lead strontiam glass was fabricated and characterized, and the absorption spectrum and upconversion spectrum of the glass were studied. The Judd-Ofelt intensity parameters Ωt (t=2, 4, 6) were found to be Ω2＝3.27×10-20 cm2, Ω4＝1.15×10-20 cm2, and Ω6＝0.38×10-20 cm2. The oscillator strength, the spontaneous transition probabilities, the fluorescence branching ratios, and excited state lifetimes were also measured and calculated. The upconversion emission intensity varies with the power of infrared excitation intensity. A plot of log Iup vs log IIR yields a straight line with slope 1.86, 1.88 and 1.85, corresponding to 525, 546, and 657 nm emission bands, respectively, which indicates that a two-photon process for the red and green emission.
其他文献
A support vector machine (SVM) with quadratic polynomial kernel function based nonlinear model one-step-ahead predictive controller is presented. The SVM based
The physical and thermal properties of P2O5-Al2O3-BaO-La2O3 glasses were investigated. The effects of glass compositions on the transition temperature, thermal
In order to estimate the feasibility of electromagnetic casting (EMC) for different metals, a mathematical model named the electromagnetic dimensionless number
研究RoHS指令中金属、非金属样品中六价铬消解的方法、步骤、注意事项.探索研究金属样品六价铬消解的最适条件及非金属消解的基本步骤,解决消解含六价铬样品的疑难问题.
通过对典型代表的200户居民和50处办公室的室内空气检测后发现宁波市的室内空气污染不可忽视。其中甲醛超标率分别为60．3％和36．0％，TVOC超标率率分别为33．8％和19．0％，苯系物超标率为5．0％左
Surface tension and filling ability of molten metal play an important role on the shaping of the molten metal. The surface tension was calculated from wetting a
La0.8 Cu0.2 MnO(3±δ) perovskite-type catalyst for methane combustion prepared through sol-gel process was characterized by X-ray Diffractometry(XRD), X-ray Ph
A nanostructured surface layer was fabricated on 1420 aluminum alloy by high-energy shot peening.Microstructures were characterized by X-ray diffractometer (XRD
The phase constitution in mixed Gd2O3 and B4C by sintering in graphite tube furnace at the temperature of 100～1489 ℃ in argon atmosphere was studied by means of
The reactive crystallization process of dexamethasone sodium phosphate was investigated in a continuous mixed-suspension, mixed-product-removal(MSMPR) crystalli