【摘 要】
：
在45钢表面激光熔覆Ni基复合涂层。利用金相显微镜、XRD衍射仪和显微硬度计研究了扫描速率对表面结构和显微硬度的影响。结果表明:不同工艺熔覆后试样均由表面熔覆区、结合区
【机 构】
：
浙江机电职业技术学院机械工程学院,
论文部分内容阅读
在45钢表面激光熔覆Ni基复合涂层。利用金相显微镜、XRD衍射仪和显微硬度计研究了扫描速率对表面结构和显微硬度的影响。结果表明:不同工艺熔覆后试样均由表面熔覆区、结合区和基体三部分组成,并达到冶金结合。复合涂层主要由FeNi3和Ni3B相组成。熔覆层显微硬度平均值都超过基体,最大硬度比基体高33%。相同激光功率条件下,扫描速度越慢,性能越好。
Laser cladding Ni-based composite coating on 45 steel surface. The effects of scanning rate on the surface structure and microhardness were investigated by metallographic microscope, XRD and microhardness tester. The results show that the samples after cladding by different processes are composed of the surface cladding zone, the bonding zone and the matrix, and the metallurgical bonding is achieved. The composite coating consists mainly of FeNi3 and Ni3B phases. The average microhardness of the cladding exceeded the matrix, and the maximum hardness was 33% higher than that of the matrix. The same laser power conditions, the slower the scan speed, the better the performance.
其他文献
１９６８年Ｇａｓｓ首先报告３例急性后极部多灶性鳞状色素上皮病变，并认为病变是原发于视网膜色素上皮（杨德旺，主编．眼科临床免疫学．北京：人民卫生出版社，１９９１．４０１）。后又有认为其眼底病变呈多发性播散性栓塞性
采用溶胶凝胶法在普通载玻片上制备了TiO2和Ag/TiO2纳米结构薄膜,利用X射线衍射仪(XRD)、X光电子能谱(XPS)、原子力显微镜(AFM)及UMT-2摩擦试验机,考察了Ag掺杂量对薄膜组成
设计人员对新材料、新产品经济性因素了解甚少，影响工程项目中的合理选用，为此，本刊不定期发布有关材料及产品的价格和参数。
Designers know very little about the economica
针对胜利褐煤焦水蒸气气化反应过程中钙组分的催化作用,在脱除矿物质胜利褐煤煤样SL+中添加CaO在1100℃热解得到添钙煤焦样品Ca-J,Ca-J经盐酸处理脱除其游离钙组分,得到添钙
通过激光熔覆在45钢表面制备出过饱和的WC增强Ni基复合涂层。对制备的复合涂层进行磨损试验,后采用MX2600FE场发射扫描电镜观察涂层磨损表面组织,发现涂层中产生了原始组织中
采用模拟轴承试验机,考察在设计的试验条件下金属磨损自修复层及其摩擦学性能.润滑剂使用含适量Mg6Si4O10(OH)8修复剂的SD/CC 40汽油机/柴油机通用油.27 h摩擦试验结束后,采
目的：探讨视网膜静脉分支阻塞（ｂｒａｎｃｈｒｅｔｉｎａｌｖｅｉｎｏｃｃｌｕｓｉｏｎ，ＢＲＶＯ）和中央静脉阻塞（ｃｅｎｔｒａｌｒｅｔｉｎａｌｖｅｉｎｏｃｃｌｕｓｉｏｎ，ＣＲＶＯ）患眼振荡电位（ｏｓｃｉｌａｔｏｒｙｐｏｔｅｎｔｉａｌｓ，ＯＰｓ）的频域和时域参数及其临床应用。方法：测定了ＢＲＶＯ９例９只眼、ＣＲＶＯ９例９只眼和４０只正常对照眼的ＯＰｓ，并经快速富里叶变换得到ＯＰｓ的频谱。对ＢＲＶＯ、ＣＲＶＯ患眼
研究化学镀液pH值、温度及施镀时间对Mg-12Li-2Al-2Zn合金表面镀镍层组织形貌和性能的影响。结果表明:在镁锂合金表面进行化学镀镍的最佳工艺参数是:pH=7±0.2,温度(80±2)℃
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥