Characterization of A-site excessive perovskite La0.7-xSmx+0.02Ca0.3CrO3-δ

来源 :稀土学报(英文版) | 被引量 : 0次 | 上传用户:laire723
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
La0.7-xSmx+0.02Ca0.3CrO3-δ(0≤x≤0.4) powders with A-site excessive perovskite structure were synthesized by auto-ignition process and characterized. X-ray diffraction (XRD) patterns of samples after sintering at 1400℃ for 4 h were indexed as tetragonal structure. The relative densities were all above 96% although decreased slightly with the increasing content of samarium, indicating that the excessive A-site element was helpful to enhance their sinterability. Conductivities of the specimens in air increased with increasing content of samar-ium. The conductivity of La0.6Sm0.12Ca0.3CrO3-δ was 33.6 S/cm in air at 700 ℃ which was about 1.7 times as high as that of La0.7Ca0.3CrO3-δ (20.1 S/cm). Average thermal expansion coefficients (TECS) of the specimens increased from 11.06×10-6 to 12.72×10-6 K-1 when x in-creased from 0 to 0.4, and they were close to that of Y doped ZrO2 (YSZ). La0.7-xSmx+0.02Ca0.3CrO(0.1≤x≤0.3) were good choices for in-termediate temperature solid oxide fuel cells (IT-SOFCs) interconnect materials.
其他文献
为了解中国新纪录种冷杉半帚霉(Leptographium abietinum)与松材线虫的关系及其致病机理,研究了冷杉半帚霉的生物学特性.菌丝生长的最适条件:温度为25℃,半光照半黑暗培养,
A new approach to prepare PbSO4 powder is studied. Using the methods of the leaching of galena concentrates in the ferric chloride media, selective purification
By using Zb4O7 and MoO4 as starting materials, ferroelectric Tb2(MoO4)3 crystal was grown by the Czochralski method. The as-grown crystal was pale green color,
U-channel forming tests were performed to investigate the surface topography evolvement of hot-dip galvanized(GI) and galvannealed(GA) steels and the effects of
The thermodynamics equilibrium principle was used to construct the diagrams for the concentration of complex ions (pc) vs pH, the distribution ratio of lead hyd
Mesostructured Ce0.6Zr0.4O2 solid solutions were synthesized by coprecipitation combined with evaporation-induced self-assembly process. The obtained materials
To illuminate the intrinsic surface activity of Zr52.5Cu17.9Ni14.6Ti5Al10 alloy in its glass and nanocrystalline states, hydrogen absorption and desorption in b
The Co3O4/acetylene black composite anodes were successfully prepared by combination of oxalate precipitation and pyrolysis of the precipitate. The composite an
Using rolling-ploughing-extrusion compound processing methods, a 3D integral-fin structure on outside surface of red copper tube with diameter of 16.0 mm and wa
Micrometer and nanometer Cr particles were co-deposited with Ni by electroplating from a nickel sulfate bath containing a certain content of Cr particles. Cr mi