The role of Nd solid-solution and grain-boundary segregation in binary NiAl alloy was studied based on microhardness and compressive macrostrain. X-ray and Auger spectra studies indicate that Nd not only is soluble in grain interiors, but also segregates to the grain boundaries. Nd solid-solution induces an increase of the microhardness from 269 to 290 HV in grain interiors and segregation results in an enhancement of hardness from 252 to 342 HV on grain boundaries. Thus, the cohesion of grain boundaries is enhanced by Nd segregation, which make the alloy doped with 0.05 wt pct Nd exhibit more compressive microstrain, i.e. the higher the compressive ductility at room temperature, the better the final surface condition at elevated temperature. Finally, a discussion was made on the reason that Nd strengthens the grain boundaries in NiAl intermetallic alloy.
The role of Nd solid-solution and grain-boundary segregation in binary NiAl alloy was studied based on microhardness and compressive macrostrain. X-ray and Auger spectra studies indicate that Nd not only is soluble in grain interiors but also segregates to the grain boundaries Nd solid-solution induces an increase of the microhardness from 269 to 290 HV in grain interiors and segregation results in an enhancement of hardness from 252 to 342 HV on grain boundaries. Thus, the cohesion of grain boundaries is enhanced by Nd segregation, which make the alloy doped with 0.05 wt pct Nd exhibit more compressive microstrain, ie the higher compressive ductility at room temperature, the better the final surface condition at elevated temperature. Finally, a discussion was made on the reason that Nd strengthens the grain boundaries in NiAl intermetallic alloy.