In this paper, the effects of test temperatures and time on the impact damage behavior of unidirectional carbon fiber reinforced epoxy resin composites, immersed in pure water, on a pendulum impact tester, was studied. The results show that immersion in liquids has a significant effect on the impact resistance of the unidirectional composite material. It is obvious that after immersion, the mass of the material increases. The fracture initiation forces as well as the fracture initiation energy decrease as the immersion time lengthens. Moreover, the higher the temperature and the longer the time are, the more the crack propagation energy and the ductility index will be. Immersion makes the fracture mode change from the dominant fiber fracture into dominant delamination. All in all, immersion decreases the impact resistance of the composites and causes the fracture mode to change.
In this paper, the effects of test temperatures and time on the impact damage behavior of unidirectional carbon fiber reinforced epoxy resin composites, immersed in pure water, on a pendulum impact tester, was studied. The results show that immersion in liquids has a significant effect on the impact resistance of the unidirectional composite material. It is obvious that after immersion, the mass of the material increases. Moreover, the mass of the material increases. longer the time are, the more the crack propagation energy and the ductility index will be. Immersion makes the fracture mode change from the dominant fiber fracture into dominant delamination. All in all, immersion decreases the impact resistance of the composites and causes the fracture mode to change.