A Composite Photoanode Based on P25/TiO2 Nanotube Arrays/Flower-Like TiO2 for High-Efficiency Dye-Se
【机 构】
：
School of Science, Wuhan University of Technology,Wuhan 430070, China;Department of Electrical and C
【出 处】
：
金属学报（英文版）
【发表日期】
：
2016年9期
其他文献
Synthetic Effects of Frequency and Duty Ratio on Growth Characteristics, Energy Consumption and Corr
The synthetic effects of frequency and duty ratio on growth characteristics and corrosion properties of coating on Ti6Al4V fabricated by microarc oxidation are investigated comprehensively.Under the condition of uniform cumulating time of positive impulse
Precipitation behavior of (Ti,V,Mo)C and microstructural evolution of the ferritic Ti-V-Mo complex microalloyed steel were investigated through changing coiling temperature (CT). It is demonstrated that the strength of the Ti-V-Mo microalloyed steel can b
The corrosion behavior of Al-5 at.％ Cr,Al-5 at.％ Si,Al-5 at.％ Mo and Al-5 at.％ Ti produced via casting and Al-5 at.％ Cr produced by high-energy ball milling and subsequent consolidation by cold pressing was studied using potentiodynamic polarization and s
Corrosion Performance of Carbon Steel in CO2 Aqueous Environment Containing Silty Sand with Differen
Corrosion performance of carbon steel in CO2 aqueous environment containing silty sand with different sizes was investigated by immersion tests and electrochemical measurements.Silty sand could form an adsorption layer on steel surface in initial period,a
The galvanic corrosion behavior of carbon fiber reinforced polymers (CFRPs) GM-CFRP and Tepex-CFRP in contact with a Zn-coated DP590 steel in solution containing 0.9 wt％ NaCl + 0.1 wt％ CaCl2 + 0.075 wt％ NaHCO3 was investigated.The results showed that the
Effect of K2TiO(C2O4)2 Addition in Electrolyte on the Microstructure and Tribological Behavior of Mi
Micro-arc oxidation (MAO) coatings with different concentrations of K2TiO(C2O4)2 in the sodium silicate base electrolyte were prepared on 6061 aluminum alloy with the aim of promoting a better understanding of the formation mechanisms and tribologicai beh
The commented paper [1] presents the results on structural, optical, and electrical properties of Zn-doped CdO thin films. Unfortunately, there are several mistakes and errors not found by any of referees. It is necessary to show these mistakes or mislead