摘要：大体积钢筋混凝土盖梁的裂缝控制问题是建筑桥梁工程中很重要的问题之一。由于裂缝的存在和发展通常会使内部的钢筋等材料产生腐蚀，降低钢筋混凝土材料的承载能力、耐久性及抗渗能力，影响建筑物的外观、使用寿命。钢筋混凝土结构破坏倒塌的工程质量事故，绝大多数是从裂缝的扩展开始的，随着裂缝的发展变化，结构构件的耐久性和适用性会不同程度的降低，严重的甚至会导致结构构件的破坏。所以研究裂缝的形态、分析裂缝产生的原因和裂缝对结构功能的影响并加以控制是一个十分重要的课题。
关键词: 现浇大体积盖梁； 裂缝； 原因； 措施
Abstract: the mass concrete cracking control of capping beam bridge engineering construction is one of the most important problems. Due to the existence and development of cracks will usually reinforced materials such as the internal corrosive, reduce the carrying capacity of reinforced concrete materials, the durability and anti-permeability ability, affect the appearance of the building, service life. Reinforced concrete structural damage collapsed engineering quality accident, the vast majority of the expansion of the cracks from start, along with the development and change of the crack, structural components and the durability of the applicability of different level will be reduced, serious can even lead to the destruction of the structure component. So the cracks, the shape of the analysis of the causes of cracks and the influence of the cracks on the structure and function to control is a very important topic.
Keywords: cast-in-situ big volume cover beam; Crack; Reason; measures
中圖分类号：TU74文献标识码：A 文章编号：
一、盖梁裂缝状态
1、 表面裂缝：分布在盖梁表面，主要是温度裂缝，一般对结构的刚度、强度危害性较小，但是影响外观质量。
2、深层裂缝：主要表现为纵、横向裂缝。部分的切断了结构断面，对盖梁结构的耐久性产生一定危害。
3、贯穿裂缝:它是由盖梁表面裂缝发展为深层裂缝，最终形成贯穿裂缝，它切断了结构的断面。破坏了结构的整体性和稳定性，其危害是比较严重的。
二、盖梁裂缝的原因
1、内外约束条件下的裂缝
混凝土内部由于水泥的水化热而形成了中心温度高，热膨胀大，中心产生了压应力，在混凝土表面产生了拉应力。若拉应力超过了混凝土的抗拉强度，混凝土将会产生裂缝。
2、塑性收缩裂缝
塑性收缩是指混凝土在凝结之前，表面因失水较快而产生的收缩。其产生的主要原因为：混凝土在终凝前几乎没有强度或强度很小，或者混凝土刚刚终凝而强度很小时，受高温或较大风力的影响，混凝土表面失水过快，造成毛细管中产生较大的负压而使混凝土体积急剧收缩，而此时混凝土的强度又无法抵抗其本身收缩，因此裂缝。
3、支撑沉陷裂缝
新浇混凝土盖梁容易在模板、支撑、地基沉陷变形的情况下产生裂缝。由于支架、支撑的刚度不足、过早拆除模板支架及施工期间的过度震动，在荷载作用下变形沉陷。沉陷变形也是混凝土盖梁裂缝产生的另一个常见原因。
4、温度裂缝
混凝土浇筑后。在混凝土内部温度由水泥水化热引起的绝对温度、浇筑温度、和散热温度叠加而成。大量热能聚积在混凝土内部而不易散发，导致内部温度急剧上升，而混凝土表面散热较快，特别是当外界温度下降的时候，就形成内外的较大温差，较大的温差造成内部与外部热胀冷缩的程度不同，使混凝土表面产生一定的温度应力，当温度应力超过混凝土的抗拉强度极限时，混凝土表面就会产生裂缝。
5、化学反应引起的裂缝
碱骨料反应裂缝和钢筋锈蚀引起的裂缝是钢筋混凝土结构中最常见的由于化学反应而引起的裂缝。
就施工因素来说，盖梁的模板、支撑变形或沉陷，混凝土的制作和捣实工艺等许多方面的施工质量问题以及缺乏养护都会增加产生裂缝或引致裂缝发展的可能性。因此，裂缝的发生和延伸与混凝土内在的特性和多种施工因素可能同时存在某种关系。也就是说，同一条裂缝的开展往往由多个原因所造成。
三、防止措施
针对裂缝产生的原因，在施工因素方面采取相应措施，以减少盖梁裂缝的产生。为此，在混凝土施工中，在材料、工序和工艺方面应当注意下列几个问题。
1、优化混凝土配合比。
（1）大体积混凝土盖梁因其水泥水化热的大量积聚，易使混凝土内外形成较大的温差，而产生温差应力，因此在满足结构强度的前提下，选用水化热较低的水泥，以降低水泥水化所产生的热量，从而控制大体积混凝土盖梁的温度升高。
（2）充分利用混凝土的中后期强度，在保证结构强度的前提下，降低水泥的用量。
（3）严格控制集料的级配及含泥量。如果含泥量大的话，不仅会增加混凝土的收缩，而且会引起混凝土抗拉强度的降低，对混凝土抗裂不利。
（4）选用合适的缓凝、减水剂等外加剂，改善混凝土的性能。加入外加剂后可以延长混凝土的凝结时间，有利于混凝土中水泥水化热量的充分散发，以降低内外温差。
（5）控制好混凝土的入模的坍落度，不宜过大，一般控制在120mm±20mm即可。
2、浇筑振捣措施
（1）采用分层浇筑混凝土，利用浇筑面积散热，以减少施工中出现裂缝的可能性。分层浇筑必须满足每一处混凝土在初凝以前就被上一层混凝土覆盖并捣实外毕。分层浇筑时还应考虑盖梁结构大小、钢筋疏密、混凝土供应情况以及水化热等因素。
（2）使用插入式振捣器应快插慢拔，插点要均匀排列，逐点移动，顺序进行，不得遗漏，做到均匀振实。移动间距不大于振捣作用半径的1.25倍（一般为300～400mm）。振捣上一层时应插入下层5～10cm，以使两层混凝土结合牢固。振捣时，振捣棒不得触及钢筋和模板。表面振动器（平板振动器）的移动间距，应保证振动器的平板覆盖已振实部分的边缘。
（3）混凝土表层设置抗裂钢筋网片，阻止应力的反射，可以有效地防止混凝土收缩产生的干裂。
3、养护措施
大体积混凝土盖梁养护的关键是保持适宜的温度和湿度。以便控制混凝土内外温差，促进混凝土强度的正常发展的同时防止混凝土裂缝的产生和发展。
(1)保持混凝土的中心温度与表面温度之间的差值小于20℃；当结构混凝土具有足够的抗裂能力的时，也不应大于25℃~30℃。混凝土拆模时，混凝土的表面温度与中心温度之间的差值不得超过20℃。
(2) 采用内部降温法来降低混凝土内外温差。内部降温法是在混凝土内部预埋水管，通冷却水（冷却在混凝土刚浇筑完成时就开始），降低混凝土的内部温度。
(3)保温法在结构外露的混凝土表面以及模板内侧覆盖保温材料（如：草袋、锯末、湿砂等），在缓慢的散热过程中，保持混凝土内外温差小于20C。根据实际情况可以延长养护时间。
结束语
大体积混凝土盖梁裂缝是混凝土结构中普遍存在的一种现象，它的出现不仅会降低建筑物的抗渗能力，影响建筑物的使用功能，而且会引起钢筋的锈蚀，混凝土的碳化，降低材料的耐久性，影响建筑物的承载能力，因此要对混凝土盖梁裂缝进行认真研究、区别对待，采用合理的方法进行处理，并在施工中采取各种有效的预防措施来预防裂缝的出现和发展，保证建筑物和构件安全、稳定地工作。
参考文献：
[1] 李立权《混凝土工手册》
[2]郭仕万，肖欣，赵和平.《混凝土施工中的裂缝控制》
关键词: 现浇大体积盖梁； 裂缝； 原因； 措施
Abstract: the mass concrete cracking control of capping beam bridge engineering construction is one of the most important problems. Due to the existence and development of cracks will usually reinforced materials such as the internal corrosive, reduce the carrying capacity of reinforced concrete materials, the durability and anti-permeability ability, affect the appearance of the building, service life. Reinforced concrete structural damage collapsed engineering quality accident, the vast majority of the expansion of the cracks from start, along with the development and change of the crack, structural components and the durability of the applicability of different level will be reduced, serious can even lead to the destruction of the structure component. So the cracks, the shape of the analysis of the causes of cracks and the influence of the cracks on the structure and function to control is a very important topic.
Keywords: cast-in-situ big volume cover beam; Crack; Reason; measures
中圖分类号：TU74文献标识码：A 文章编号：
一、盖梁裂缝状态
1、 表面裂缝：分布在盖梁表面，主要是温度裂缝，一般对结构的刚度、强度危害性较小，但是影响外观质量。
2、深层裂缝：主要表现为纵、横向裂缝。部分的切断了结构断面，对盖梁结构的耐久性产生一定危害。
3、贯穿裂缝:它是由盖梁表面裂缝发展为深层裂缝，最终形成贯穿裂缝，它切断了结构的断面。破坏了结构的整体性和稳定性，其危害是比较严重的。
二、盖梁裂缝的原因
1、内外约束条件下的裂缝
混凝土内部由于水泥的水化热而形成了中心温度高，热膨胀大，中心产生了压应力，在混凝土表面产生了拉应力。若拉应力超过了混凝土的抗拉强度，混凝土将会产生裂缝。
2、塑性收缩裂缝
塑性收缩是指混凝土在凝结之前，表面因失水较快而产生的收缩。其产生的主要原因为：混凝土在终凝前几乎没有强度或强度很小，或者混凝土刚刚终凝而强度很小时，受高温或较大风力的影响，混凝土表面失水过快，造成毛细管中产生较大的负压而使混凝土体积急剧收缩，而此时混凝土的强度又无法抵抗其本身收缩，因此裂缝。
3、支撑沉陷裂缝
新浇混凝土盖梁容易在模板、支撑、地基沉陷变形的情况下产生裂缝。由于支架、支撑的刚度不足、过早拆除模板支架及施工期间的过度震动，在荷载作用下变形沉陷。沉陷变形也是混凝土盖梁裂缝产生的另一个常见原因。
4、温度裂缝
混凝土浇筑后。在混凝土内部温度由水泥水化热引起的绝对温度、浇筑温度、和散热温度叠加而成。大量热能聚积在混凝土内部而不易散发，导致内部温度急剧上升，而混凝土表面散热较快，特别是当外界温度下降的时候，就形成内外的较大温差，较大的温差造成内部与外部热胀冷缩的程度不同，使混凝土表面产生一定的温度应力，当温度应力超过混凝土的抗拉强度极限时，混凝土表面就会产生裂缝。
5、化学反应引起的裂缝
碱骨料反应裂缝和钢筋锈蚀引起的裂缝是钢筋混凝土结构中最常见的由于化学反应而引起的裂缝。
就施工因素来说，盖梁的模板、支撑变形或沉陷，混凝土的制作和捣实工艺等许多方面的施工质量问题以及缺乏养护都会增加产生裂缝或引致裂缝发展的可能性。因此，裂缝的发生和延伸与混凝土内在的特性和多种施工因素可能同时存在某种关系。也就是说，同一条裂缝的开展往往由多个原因所造成。
三、防止措施
针对裂缝产生的原因，在施工因素方面采取相应措施，以减少盖梁裂缝的产生。为此，在混凝土施工中，在材料、工序和工艺方面应当注意下列几个问题。
1、优化混凝土配合比。
（1）大体积混凝土盖梁因其水泥水化热的大量积聚，易使混凝土内外形成较大的温差，而产生温差应力，因此在满足结构强度的前提下，选用水化热较低的水泥，以降低水泥水化所产生的热量，从而控制大体积混凝土盖梁的温度升高。
（2）充分利用混凝土的中后期强度，在保证结构强度的前提下，降低水泥的用量。
（3）严格控制集料的级配及含泥量。如果含泥量大的话，不仅会增加混凝土的收缩，而且会引起混凝土抗拉强度的降低，对混凝土抗裂不利。
（4）选用合适的缓凝、减水剂等外加剂，改善混凝土的性能。加入外加剂后可以延长混凝土的凝结时间，有利于混凝土中水泥水化热量的充分散发，以降低内外温差。
（5）控制好混凝土的入模的坍落度，不宜过大，一般控制在120mm±20mm即可。
2、浇筑振捣措施
（1）采用分层浇筑混凝土，利用浇筑面积散热，以减少施工中出现裂缝的可能性。分层浇筑必须满足每一处混凝土在初凝以前就被上一层混凝土覆盖并捣实外毕。分层浇筑时还应考虑盖梁结构大小、钢筋疏密、混凝土供应情况以及水化热等因素。
（2）使用插入式振捣器应快插慢拔，插点要均匀排列，逐点移动，顺序进行，不得遗漏，做到均匀振实。移动间距不大于振捣作用半径的1.25倍（一般为300～400mm）。振捣上一层时应插入下层5～10cm，以使两层混凝土结合牢固。振捣时，振捣棒不得触及钢筋和模板。表面振动器（平板振动器）的移动间距，应保证振动器的平板覆盖已振实部分的边缘。
（3）混凝土表层设置抗裂钢筋网片，阻止应力的反射，可以有效地防止混凝土收缩产生的干裂。
3、养护措施
大体积混凝土盖梁养护的关键是保持适宜的温度和湿度。以便控制混凝土内外温差，促进混凝土强度的正常发展的同时防止混凝土裂缝的产生和发展。
(1)保持混凝土的中心温度与表面温度之间的差值小于20℃；当结构混凝土具有足够的抗裂能力的时，也不应大于25℃~30℃。混凝土拆模时，混凝土的表面温度与中心温度之间的差值不得超过20℃。
(2) 采用内部降温法来降低混凝土内外温差。内部降温法是在混凝土内部预埋水管，通冷却水（冷却在混凝土刚浇筑完成时就开始），降低混凝土的内部温度。
(3)保温法在结构外露的混凝土表面以及模板内侧覆盖保温材料（如：草袋、锯末、湿砂等），在缓慢的散热过程中，保持混凝土内外温差小于20C。根据实际情况可以延长养护时间。
结束语
大体积混凝土盖梁裂缝是混凝土结构中普遍存在的一种现象，它的出现不仅会降低建筑物的抗渗能力，影响建筑物的使用功能，而且会引起钢筋的锈蚀，混凝土的碳化，降低材料的耐久性，影响建筑物的承载能力，因此要对混凝土盖梁裂缝进行认真研究、区别对待，采用合理的方法进行处理，并在施工中采取各种有效的预防措施来预防裂缝的出现和发展，保证建筑物和构件安全、稳定地工作。