The effect of thermal exposure on the microstructure and creep properties of the Ni-based single crystal superalloy in different test conditions was studied. Lo
【机 构】
：
School of Materials and Chemical Engineering,Xi’an Technological University,Xi’an 710021,China;Fugu
论文部分内容阅读
The effect of thermal exposure on the microstructure and creep properties of the Ni-based single crystal superalloy in different test conditions was studied. Long-term exposure was performed at 1,000 ℃ and 1,100 ℃ for 500 h prior to the creep tests. The creep lifetime is found to be improved after the long-term exposure at 1,000 ℃ for 500 h as a result of the formation of secondary M23C6 in the interdendritic region. The coarsening of γ' precipitates accompanied by the formation of TCP phase lead to the degradation of alloy, which is responsible for the reduction of the creep lifetime of Ni-base single crystal superalloy after long-term exposure at 1,100 ℃ for 500 h. The creep lifetime of 1,000 ℃ thermally exposed sample under the conditions of 1,093 ℃/137 MPa is lower than that of heat-treated state. Thermal exposure at 1,100 ℃ for 500 h causes the creep lifetime to drop drastically.
其他文献
日前,涂料行业资深专家段质美先生收集了鲜有报道的行业前辈戴济先生的生平事迹和资料,对于重新认识中国近现代涂料工业的早期贡献者做了一些考证并撰写了此文,并提出戴济作为中国涂料业的先驱实至名归。希望本文刊出后能引起行业关注,也欢迎进行探讨,以达到行业共识。
Large-size primary MC carbides can significantly reduce the performance of M2 high-speed steel. To better control the morphology and size of primary MC carbides
This work aims to produce a high manganese steel with more refined austenite grains and better wear resistance without sacrificing the toughness and tensile properties by Mn alloying and Ti ladle treatment in comparision to ASTM A128 Gr.E1 steel (1.0C-13M
A Mn18Cr2 steel containing TiN precipitates was fabricated by vacuum induction melting.The morphology of TiN precipitates and the interface orientation relationship between TiN and γ-Fe were characterized by means of SEM,TEM and SAED,and the formation mec
The effect of a low-frequency alternating magnetic field (AMF,0 A 0 Hz,5 A 10 Hz,10 A 10 Hz,15 A 10 Hz) on the hot tearing susceptibility (HTS) of a magnesium alloy (EV31) was systematically studied using a combination of experiment and numerical simulati
K416B Ni-based superalloy with high W content has good high temperature properties and low cost, which has a great development potential. To investigate the roo
Inconel 718 alloys were fabricated by selective laser melting under different scanning speeds to investigate the change of the morphology of molten pool, direct
Seeking high-performance computing methods to solve the problem of a large amount of calculation, low calculation efficiency, and small simulation scale on the
In this work,a new(Y,Gd)H2 precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg
Al-5Ti-B and Al-5Ti-B-Gd master alloy refiners were fabricated by fluorine salt casting method. The microstructure and phase constitution of the master alloys w